SABIC Innovative Plastics LNP STAT-LOY A3000LTH ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY A3000LTH ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-LOY* A3000LTH is a compound based on ABS resin. Added features of this material include: Transparent, Antistatic, Formulation Locked.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.520 % | 0.520 % | 50% RH, 24 hrs; ASTM D570 |
| 0.800 % | 0.800 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 27.0 MPa | 3920 psi | Type I, 5 mm/min; ASTM D638 |
| 28.0 MPa | 4060 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
| 38.0 MPa | 5510 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 33 % | 33 % | Type I, 5 mm/min; ASTM D638 |
| 37 % | 37 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.8 % | 3.8 % | 5 mm/min; ISO 527 |
| 3.9 % | 3.9 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1 mm/min; ISO 527 |
| 1.68 GPa | 244 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 52.0 MPa | 7540 psi | ISO 178 |
| Flexural Yield Strength | 56.0 MPa | 8120 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.56 GPa | 226 ksi | 2 mm/min; ISO 178 |
| 1.66 GPa | 241 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 34.0 J @Temperature 23.0 °C |
25.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 26.0 J | 19.2 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 106 µm/m-°C @Temperature -30.0 - 30.0 °C |
58.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 113 µm/m-°C @Temperature -30.0 - 30.0 °C |
62.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 °C | 169 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 78.0 °C @Thickness 3.20 mm |
172 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 65.0 °C @Thickness 3.20 mm |
149 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Packaging 2188GC-3V Polyvinyl Chloride, Rigid (PVC, Rigid)
- SABIC Innovative Plastics Cycoloy® XCY630 PC+ABS (Europe-Africa-Middle East)
- PlastiComp Complet® LCF10/LGF30 - PP Polypropylene, 40% Long Carbon/Glass Fiber
- Eastman Tenite 371A-12 CAP Cellulose Acetate Propionate (discontinued **)
- Lehmann & Voss LUVOCOM® 50-7586 Polycarbonate, with carbon fiber
- Teknor Apex Sinvicomp SIC 3707 Polyvinyl Chloride, Rigid
- Silberline Sparkle Silver® Premier 561
- Lubrizol Estane® ZHF 82AT0 Thermoplastic Polyurethane, Flame Retardant
- Unitika CX-2500 PA6, Conditioned
- Beijing Ranger Chem WAR6101 Semi Solid Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved