- A. Schulman SCHULAMID® 66 MK20HI 20% Mineral Reinforced, Impact Modified Nylon 66
A. Schulman SCHULAMID® 66 MK20HI 20% Mineral Reinforced, Impact Modified Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Mineral Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 66 MK20HI 20% Mineral Reinforced, Impact Modified Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.015 cm/cm @Thickness 3.175 mm |
0.0050 - 0.015 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.3 MPa | 10200 psi | ASTM D638 |
| Tensile Modulus | 3.499 GPa | 507.5 ksi | ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 295 - 305 °C | 563 - 581 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- RheTech Products GC10P200-01 10% Glass Fiber Reinforced Polypropylene Copolymer, Non-UV Stabilized, Chemically Coupled, Black
- PolyOne Dynaflex™ G7930-9 NSFG Thermoplastic Elastomer (TPE)
- Quantum Composites QC-2130 Phenolic 25% Glass Fiber SMC (discontinued **)
- Firestone C200-001 Nylon 6
- Karina E 1000/0085-IE MBPEB White Color Concentrate
- Westlake Plastics Propylux® 290 Polypropylene, Heat Stabilized
- A. Schulman POLYBATCH™ White LL8350 AP Concentrate Based In LLDPE
- ExxonMobil LD 117.85 Blown Overwrap Film Resin
Copyright © lookpolymers.com All Rights Reserved