Polymer Property : Drying Temperature = 130 °C Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Processing Properties	Metric	English	Comments
Drying Temperature	130 - 150 °C	266 - 302 °F	Average value: 148 °C Grade Count:8
Overview of materials for Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler". Specific grades with carbon fiber content bet..
Drying Temperature	130 Â°C	266 Â°F	Injection Molding
LG Chemical LupoxÂ® GP2056F PBT+GF5% Description: Injection Molding, PBT+GF5%, Flame Retardant Application: IT/OA, E&E (Connector)CAS No. 71342-77-3, 65997-17-3, 24968-12-5 and 1309-64-4Information provided by LG Chemical
Drying Temperature	130 - 150 Â°C @Time 10800 sec	266 - 302 Â°F @Time 3.00 hour
LATI Larton L K/20 L-PPS, 20% Carbon Fiber Reinforced Linear Polyphenylene Sulfide (L-PPS) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle..
Drying Temperature	130 °C	266 °F
A. Schulman SCHULADUR® A GF33HI 33% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman.
Drying Temperature	130 °C	266 °F
A. Schulman ComAlloy® E-13370 Lubricated Reinforced Polyester Alloy Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Drying Temperature	130 °C	266 °F
A. Schulman VOLOY™ 462 Hybrid Reinforced PBT Alloy Information provided by A. Schulman.
Drying Temperature	130 °C	266 °F
A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT Information provided by A. Schulman.
Drying Temperature	130 - 140 °C @Time 14400 sec	266 - 284 °F @Time 4.00 hour
Zhejiang Juner 301-G30 30% Glass Fibre Reinforced and Flammable Resistant Applications: Electrons and Electricity: TV Components, Plugs of Computers, Exhaust Fans of Computers, Plugs, Sockets, Shells of Electronics, Framework of Level Output Transformers, Pipe Pedestals, ..
Drying Temperature	130 °C	266 °F
A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman.
Drying Temperature	130 °C	266 °F
A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT Information provided by A. Schulman.
Drying Temperature	130 °C	266 °F
A. Schulman SCHULADUR® B GF30 30% Glass Fiber Reinforced PET Information provided by A. Schulman.
Drying Temperature	130 °C	266 °F
A. Schulman COMTUF® 420 Impact Modified PBT Information provided by A. Schulman.
Drying Temperature	130 °C	266 °F
A. Schulman SCHULADUR® B GF30 30% Glass Fiber Reinforced PET Information provided by A. Schulman.
Drying Temperature	130 °C	266 °F
A. Schulman COMTUF® 462 Glass/Fiber Mineral Reinforced, Impact Modified PET Alloy Information provided by A. Schulman.
Drying Temperature	130 °C	266 °F
A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT Information provided by A. Schulman.
Drying Temperature	130 °C	266 °F
Beijing Chemical Industry KAIFA® 201-G15R PBT Resin 20% glass fiber reinforced, good flow and toughnessInformation provided by Beijing Chemical Industry Research Institute (Group)
Drying Temperature	130 °C	266 °F
Beijing Chemical Industry KAIFA® 201-G30R PBT Resin 30% glass fiber reinforced, good flow and toughnessInformation provided by Beijing Chemical Industry Research Institute (Group)
Drying Temperature	130 °C	266 °F
Beijing Chemical Industry KAIFA® 301-G20F PBT Resin 20% glass fiber reinforced, flame retardant, good flow, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group)
Drying Temperature	130 °C	266 °F
Beijing Chemical Industry KAIFA® HN201-G30 PA6 Resin 30% glass fiber reinforced, thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group)
Drying Temperature	130 °C	266 °F
Beijing Chemical Industry KAIFA® MN301-M30 Nylon 66 Resin Mineral filled, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group)
Drying Temperature	130 - 150 °C @Time 10800 sec	266 - 302 °F @Time 3.00 hour
LATI Latilub 80-15T G/30 PPS, 30% Glass Fiber Reinforced, PTFE Filled Self-lubricating product based on Polyphenylene Sulfide (PPS). PTFE. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I..
Drying Temperature	130 - 150 °C @Time 10800 sec	266 - 302 °F @Time 3.00 hour
LATI Latilub 80-17ST G/30 PPS, 30% Glass Fiber Reinforced, Silicone/PTFE Filled Self-lubricating product based on Polyphenylene Sulfide (PPS). Silicone / PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provid..