A. Schulman SCHULADUR® A GF33HI 33% Glass Fiber Reinforced, High Impact PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULADUR® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULADUR® A GF33HI 33% Glass Fiber Reinforced, High Impact PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.175 mm |
0.0020 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117.39 MPa | 17026 psi | ASTM D638 |
| Flexural Strength | 181.5 MPa | 26320 psi | ASTM D790 |
| Flexural Modulus | 8.063 GPa | 1169 ksi | ASTM D790 |
| Izod Impact, Notched | 1.51 J/cm | 2.82 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 252 - 260 °C | 485 - 500 °F | |
| Mold Temperature | 30.0 - 65.6 °C | 86.0 - 150 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene Latice® 2620 Acrylonitrile-Butadiene Copolymer
- Omya OMYAFLOW® F - SY Calcium Carbonate
- Palm Labs Adhesives TURBO FUSE SERIES 170 LOW ODOR/LOW BLOOM (1500 Viscosity) Rapid Bonding Adhesive
- PolyOne Geon™ L4605 Green 5765 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid)
- Lehmann & Voss LUVOCOM® 1/GF/30/TF/15/HS/BK Polyamide 66, with glass fiber and PTFE, heat stabilized
- Wieland Porta Oprimum 710 Solder
- EMS-Grivory Grivory® HT1V-45 HY black 9205 PA6T/6I-GF45
- Asahi Kasei Thermylene® P6-20FG-1740 20% Glass Fiber Reinforced, High Impact
- Bayshore Vinyl Compounds BVC 1204-70 Clear Vinyl Compound
- Plastcom SLOVAMID 6 FRC 2 TS PA6, flame retardant, heat stability
Copyright © lookpolymers.com All Rights Reserved