A. Schulman ComAlloy® E-13370 Lubricated Reinforced Polyester Alloy
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy® E-13370 Lubricated Reinforced Polyester Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.175 mm |
0.0020 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 104 MPa | 15100 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
| Flexural Modulus | 7.888 GPa | 1144 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.45 J/cm | 10.2 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 227 °C | 441 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 65.0 - 95.0 °C | 149 - 203 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- BASF Capron® B100ZP Nylon 6 (DAM) (discontinued **)
- Saint-Gobain Chemfab® SlipGrip™ 3 PTFE/Silicone Coated Fiberglass Fabric
- Lubrizol ESTANE® T4086 Ester Based Thermoplastic Polyurethane (European Grade)
- A. Schulman COMTUF® 5011 10% Glass Fiber Reinforced Polycarbonate
- DuPont™ Nomex® 418 Paper, 10 mil Nominal Thickness
- 3M RPF-C (0.32 g/cc) (Reinforced Polyurethane Foam) Continuous Strand Fiberglass
- Polyram RamOfin PPC104 Polypropylene Copolymer
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 482°C Temper
Copyright © lookpolymers.com All Rights Reserved