Beijing Chemical Industry KAIFA® HN201-G30 PA6 Resin
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® HN201-G30 PA6 Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass fiber reinforced, thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 135 MPa | 19600 psi | ASTM D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm @Thickness 3.20 mm |
0.749 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Charpy Impact Unnotched | 7.80 J/cm² | 37.1 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Strength | 23.0 kV/mm @Thickness 2.00 mm |
584 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 220 °C | 410 - 428 °F | |
| Middle Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |
| Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | |
| Nozzle Temperature | 240 - 245 °C | 464 - 473 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi |
Users viewing this material also viewed the following:
- Greene Tweed Arlon® 1000 Polyketone
- Lanxess Durethan® BKV 130 CS DUS008 600091 Nylon 6, 30% Glass Fiber
- Saint-Gobain Chemlam® Silver 12 Wear Resistant Industrial Laminate
- Saint-Gobain CHR® K290ESD Polyimide Film Backing Silicone Adhesive Pressure Sensitive Tape
- Total PSC 535 Polystyrene
- DuPont Performance Polymers Minlon® 22C NC010 Nylon 66 (Unverified Data**)
- ArcelorMittal AS80 Aluminized steel
- Solvay Specialty Polymers Solef® 11010 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
- Polimeri Europa Europrene® N 2845 Acrylonitrile-Butadiene Rubber
- PolyOne Gravi-Tech™ GRV-TP-050-CU-NAT Styrene Butadiene Block Copolymer (SBC)
Copyright © lookpolymers.com All Rights Reserved