Overview of materials for Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler". Specific grades with carbon fiber content between 35% and 44% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.48 - 1.60 g/cc
0.0535 - 0.0578 lb/in³
Average value: 1.52 g/cc Grade Count:12
Filler Content 40.0 %
40.0 %
Average value: 40.0 % Grade Count:10
Water Absorption 0.0200 %
0.0200 %
Average value: 0.0200 % Grade Count:3
Linear Mold Shrinkage 0.000500 - 0.00200 cm/cm
0.000500 - 0.00200 in/in
Average value: 0.000692 cm/cm Grade Count:11
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 77.2 - 234 MPa
11200 - 34000 psi
Average value: 175 MPa Grade Count:12
100 - 160 MPa

@Temperature 60.0 - 150 °C
14500 - 23200 psi

@Temperature 140 - 302 °F
Average value: 131 MPa Grade Count:1
Elongation at Break 0.000 - 1.20 %
0.000 - 1.20 %
Average value: 0.846 % Grade Count:12
0.500 - 1.20 %

@Temperature 60.0 - 150 °C
0.500 - 1.20 %

@Temperature 140 - 302 °F
Average value: 0.875 % Grade Count:1
Modulus of Elasticity 12.4 - 45.0 GPa
1800 - 6530 ksi
Average value: 33.5 GPa Grade Count:11
15.0 - 42.0 GPa

@Temperature 60.0 - 150 °C
2180 - 6090 ksi

@Temperature 140 - 302 °F
Average value: 29.5 GPa Grade Count:1
Flexural Yield Strength 126 - 317 MPa
18300 - 46000 psi
Average value: 249 MPa Grade Count:11
Flexural Modulus 11.0 - 31.0 GPa
1600 - 4500 ksi
Average value: 26.6 GPa Grade Count:11
Izod Impact, Notched 0.278 - 0.641 J/cm
0.520 - 1.20 ft-lb/in
Average value: 0.508 J/cm Grade Count:10
Izod Impact, Unnotched 1.60 - 4.86 J/cm
3.00 - 9.10 ft-lb/in
Average value: 3.59 J/cm Grade Count:9
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 260 - 280 °C
500 - 536 °F
Average value: 267 °C Grade Count:3
Deflection Temperature at 1.8 MPa (264 psi) 260 - 270 °C
500 - 518 °F
Average value: 265 °C Grade Count:11
Flammability, UL94 V-0
V-0
Grade Count:10
Electrical Properties Metric English Comments
Electrical Resistivity 10.0 ohm-cm - 1e+05
10.0 ohm-cm - 1e+05
Average value: 626 ohm-cm Grade Count:10
Processing Properties Metric English Comments
Melt Temperature 290 - 329 °C
554 - 625 °F
Average value: 316 °C Grade Count:8
Mold Temperature 130 - 177 °C
266 - 350 °F
Average value: 154 °C Grade Count:10
Drying Temperature 130 - 150 °C
266 - 302 °F
Average value: 148 °C Grade Count:8
Moisture Content 0.0400 %
0.0400 %
Average value: 0.0400 % Grade Count:7
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:9