- A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT
A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULADUR® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.175 mm |
0.0030 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 128 MPa | 18500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 8.62 GPa | 1250 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.81 J/cm | 16.5 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 30.0 - 65.6 °C | 86.0 - 150 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Polymer Resources PPX-EN-FR3 Modified-PPO, V-1 Flame Retardant, Extrusion Grade
- BASF Capron® 8230G HS 6% Glass-Filled Nylon 6 (Dry) (discontinued **)
- Kingfa PA6-MG45 45% Glass & Mineral Filled PA6
- Solvay Specialty Polymers Ixan® PVS 706 Polyvinylidene Chloride (PVDC)
- SMAC SMACWRAP® EX Damping Material, 0.12 mm
- Master Bond EP112 Low Viscosity Heat Curing Cycloaliphatic Epoxy Adhesive
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 2.0 PHR Di-Cup 40C
- ALM PA 850 Black Nylon 11 SLS Prototyping Polymer
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N330 Filler
Copyright © lookpolymers.com All Rights Reserved