LATI Larton L K/20 L-PPS, 20% Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler
Manufacturer LATI
Trade Name Larton
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larton L K/20 L-PPS, 20% Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Linear Polyphenylene Sulfide (L-PPS) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0020 - 0.0030 cm/cm
0.0020 - 0.0030 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa

@Temperature 150 °C
 6530 psi

@Temperature 302 °F
65.0 MPa

@Temperature 120 °C
 9430 psi

@Temperature 248 °F
95.0 MPa

@Temperature 90.0 °C
 13800 psi

@Temperature 194 °F
125 MPa

@Temperature 60.0 °C
 18100 psi

@Temperature 140 °F
145 MPa

@Temperature 23.0 °C
 21000 psi

@Temperature 73.4 °F
Elongation at Break 1.0 %

@Temperature 23.0 °C
 1.0 %

@Temperature 73.4 °F
1.2 %

@Temperature 60.0 °C
 1.2 %

@Temperature 140 °F
1.5 %

@Temperature 90.0 °C
 1.5 %

@Temperature 194 °F
1.9 %

@Temperature 120 °C
 1.9 %

@Temperature 248 °F
2.1 %

@Temperature 150 °C
 2.1 %

@Temperature 302 °F
Tensile Modulus 7.50 GPa

@Temperature 150 °C
 1090 ksi

@Temperature 302 °F
9.20 GPa

@Temperature 120 °C
 1330 ksi

@Temperature 248 °F
12.5 GPa

@Temperature 90.0 °C
 1810 ksi

@Temperature 194 °F
15.8 GPa

@Temperature 60.0 °C
 2290 ksi

@Temperature 140 °F
18.0 GPa

@Temperature 23.0 °C
 2610 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 1.80 J/cm²
8.57 ft-lb/in²
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Volume Resistivity 8000 ohm-cm
8000 ohm-cm
Surface Resistance 2000 ohm
2000 ohm
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 130 - 140 °C
266 - 284 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
 266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Users viewing this material also viewed the following: