A. Schulman VOLOY™ 462 Hybrid Reinforced PBT Alloy
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman VOLOY™ 462 Hybrid Reinforced PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.175 mm |
0.0020 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 101 MPa | 14700 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 149 MPa | 21600 psi | ASTM D790 |
| Flexural Modulus | 8.701 GPa | 1262 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.86 J/cm | 9.10 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 65.0 - 95.0 °C | 149 - 203 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Termopol Termoton® K2GA5080A TPE Compound, based on SEBS and Polyolefins
- IDI Composites A-203 Thermoset Polyester, Sheet
- Teknor Apex MF 141 Polyvinyl Chloride, Flexible Film
- DuPont Elvax® 3135SB Ethylene-Vinyl Acetate Copolymer Resin for Blown Film
- Master Bond UV15DC80 One Component, UV and Heat Curable Epoxy System
- Lubrizol Estane® 58144 Thermoplastic Polyurethane
- Braskem TI4040WT Impact Copolymer Polypropylene
- Bapolene® 3039U Polyethylene, Rotational Molding Grade
- 3M AC-730 Class B-1/2 Aerospace Sealant
- Axiall 18650 Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved