A. Schulman SCHULADUR® B GF30 30% Glass Fiber Reinforced PET
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULADUR® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULADUR® B GF30 30% Glass Fiber Reinforced PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0019 cm/cm @Thickness 3.175 mm |
0.0019 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Strength | 221 MPa | 32000 psi | ASTM D790 |
| Flexural Modulus | 9.65 GPa | 1400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.41 J/cm | 12.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 254 °C | 489 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 246 °C | 475 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 226 °C | 438 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 90.0 - 110 °C | 194 - 230 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Proto3000 Objet RGD525 High Temperature Prototyping Polymer
- Teknor Apex Telcar® TL-1520C Thermoplastic Elastomer
- Thermoseal RG-N120 PTG Gasketing
- A. Schulman PP 2268-01 Polypropylene High Flow, Impact Copolymer Polypropylene
- DuPont Appeel® LSR20D751 Lidding Sealant Resin
- CIMBAR RMF 75 Recycled Mineral Filler
- Eurostar Starpylen HU 70E3 HDPE, Injection Molding
- Azoty Tarnow™ TARFLEN SG-1 PTFE
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Molded
- SABIC Innovative Plastics LNP VERTON NV008E PC/ABS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved