- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 221 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 221 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C @Thickness 3.18 mm |
221 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Stat-Tech™ AT-CB2/000 CR Acetal (POM) Copolymer Stat-Tech™ AT-CB2/000 CR XP020229R2Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® CU1650 PC+ABS (Europe-Africa-Middle East) UV stabilized, non-FR PC/ABS of excellent flow and impact performanceThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPC GF5030 PD2 Polypropylene Copolymer, Glass Fiber Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® CY100FC PC+ABS High impact PC+ABS material designed for local Pacific Automotive applications |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® CY9640 PC+ABS (Asia Pacific) PC+ ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® CY9640 PC+ABS (Europe-Africa-Middle East) PC+ ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat AgingThis data was supplied by SABIC-IP for the Europe-Africa-Middle East r.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® CY9650 PC+ABS (Asia Pacific) PC+ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat AgingThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycoloy® XCY620 PC+ABS (Asia Pacific) PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ASTM D648 |
| Polymer Resources TP-FV699 PBT, 10% Glass Reinforced Structural Foam Grade, Low Shrinkage Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C @Thickness 3.20 mm |
221 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP FARADEX NS003 PC+ABS LNP* FARADEX* NS003 is a compound based on PC+ABS resin containing 15% Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ASTM D648 |
| Shell Carilon® D26FX100 Polyketone, General-Purpose Extrusion Grade
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer D26FX100 is a general-purpose extrusion grade with mechanical properties that classify it as an eng.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C @Thickness 6.35 mm |
221 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Covestro Bayblend® KU2-1500 Polycarbonate + ABS Blend, Extrusion/Blow-Molding
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75 |
| Manifattura Cattaneo PVDF Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C @Thickness 3.17 mm |
221 °F @Thickness 0.125 in |
ASTM D648 |
| Metton LMR M1539 Liquid Molding Resin Metton LMR is a tough and durable engineering plastic material used to produce large or thick molded parts for many diversified applications. The Metton LMR reaction injection molding process can .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Xenoy® X5410 PC+PET (Europe-Africa-Middle East) Mineral filled PC+PET resin with high heat dimensional stability for paint systems. It has very low CTE and excellent flow - impact balance for automotive exterior applications, like body panels, ta.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75-1/-2 |
| Styrolution Luran® S KR 2864 C Colored ASA+PC Description: Easy flowing injection molding grade with heat resistance for parts with thin walls and/or with adverse flowpath/wall thickness ratios.Applications: Mobile phone housings.Information pr.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP NX07354 PC+ABS (Asia Pacific) This is a PC/ABS compound, a good candidate for Laser Direct Structuring applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | unannealed; ISO 75 A |
| Styron Pulse® A35-105 PC/ABS PULSE™ A35-105 engineering resins give exceptional impact strength even at low temperatures and have high heat distortion temperature.Information provided by DowThis product line was spun off f.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C @Thickness 6.40 mm |
221 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL N1050 PPE+HIPS (Asia Pacific) Noryl* N1050 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR ad.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75 |
| Wellman Wellamid® GS40-66 22L-N 40% Glass Sphere Filled Nylon 66, Lubricated Typical Applications: Potentiometer liners, electrical coil forms, automotive window lift and power door lock switch bodies, gears, thick wall section moldings, emission control valves.Data provided.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® GTR 45 PA6I/6T Product description: Grivory GTR 45 is a transparent engineering thermoplastic based on amorphous, partially aromatic copolyamide for injection molding. Compared to other semi crystalline polyamides.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ASTM D648, ISO 75 |
| EPICHEM Epiryl B PPO Polyphenylene oxide |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75-2 |
| BASF Ultradur® S 4090 G2 10% Glass Filled PBT Description: Is a PBT + ASA, easy-flowing injection-molding grades with 10% glass fibers; for rigid, tough and dimensionally stable technical parts e. g. housings, consoles, contact carriers, covers.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron IMG-1115 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C @Thickness 6.40 mm |
221 °F @Thickness 0.252 in |
Method A; ASTM D648 |
| Bhansali Engineering Abstron KU602L ABS Heat Resistant High rigidityInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 - 115 °C | 221 - 239 °F | ASTM D648 |
| Arkema Group KYNAR® 740-02 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mecha.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ASTM D648 |
| E-Polymers Tekaloy® S630X , High Impact, Weather Resistance, Chemical Resistance PC/PBT Alloy High impact, weather resistance, chemical resistanceInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ASTM D648 |
| Ashley Polymers Ashlene® PC/ABS Alloy 306 General purpose with high impact, good low temperature properties and high heat resistance.Data provided by the manufacturer |
|||