BASF Ultradur® S 4090 G2 10% Glass Filled PBT

Category Polymer , Thermoplastic , ASA Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced
Manufacturer BASF
Trade Name Ultradur®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur® S 4090 G2 10% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Is a PBT + ASA, easy-flowing injection-molding grades with 10% glass fibers; for rigid, tough and dimensionally stable technical parts e. g. housings, consoles, contact carriers, covers.Information provided by BASF
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
Saturation; DIN 53495/1L
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C; 50% RH
Viscosity Measurement 105
105
[ml/g]; Viscosity number; ISO 1628
70

@Temperature 290 °C
 70

@Temperature 554 °F
 20 mins plasticating
75

@Temperature 300 °C
 75

@Temperature 572 °F
 10 mins plasticating
75

@Temperature 280 °C
 75

@Temperature 536 °F
 30 mins plasticating
90

@Temperature 270 °C
 90

@Temperature 518 °F
 30 mins plasticating
95

@Temperature 290 °C
 95

@Temperature 554 °F
 10 mins plasticating
100

@Temperature 260 °C
 100

@Temperature 500 °F
 30 mins plasticating
100

@Temperature 300 °C
 100

@Temperature 572 °F
 5 mins plasticating
105

@Temperature 280 °C
 105

@Temperature 536 °F
 10 mins plasticating
106

@Temperature 250 °C
 106

@Temperature 482 °F
 30 mins plasticating
110

@Temperature 270 °C
 110

@Temperature 518 °F
 10 mins plasticating
115

@Temperature 260 °C
 115

@Temperature 500 °F
 10 mins plasticating
115

@Temperature 240 °C
 115

@Temperature 464 °F
 30 mins plasticating
117

@Temperature 250 °C
 117

@Temperature 482 °F
 10 mins plasticating
120

@Temperature 240 °C
 120

@Temperature 464 °F
 10 mins plasticating
Linear Mold Shrinkage, Flow 0.0046 cm/cm
0.0046 in/in
Sheet
Linear Mold Shrinkage, Transverse 0.0085 cm/cm
0.0085 in/in
Sheet
Melt Flow 45.85 g/10 min

@Load 2.16 kg,
Temperature 275 °C
 45.85 g/10 min

@Load 4.76 lb,
Temperature 527 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 140 MPa
20300 psi
ISO 2039-1
Tensile Strength 35.0 MPa

@Temperature 100 °C
 5080 psi

@Temperature 212 °F
 ISO 527
60.0 MPa

@Temperature 50.0 °C
 8700 psi

@Temperature 122 °F
 ISO 527
80.0 MPa

@Temperature 23.0 °C
 11600 psi

@Temperature 73.4 °F
 ISO 527
115 MPa

@Temperature -40.0 °C
 16700 psi

@Temperature -40.0 °F
 ISO 527
Tensile Strength, Yield 75.0 MPa
10900 psi
50 mm/min; ISO 527-2
Elongation at Yield 2.9 %
2.9 %
50 mm/min; ISO 527-2
Modulus of Elasticity 4.50 GPa
653 ksi
ISO 527-2
Flexural Strength 119 MPa
17300 psi
ISO 178
Charpy Impact Unnotched 2.70 J/cm²

@Temperature -30.0 °C
 12.8 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
4.50 J/cm²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Dart Drop, Total Energy 5.00 J
3.69 ft-lb
W<sub>501</sub> housing; ISO 6603-1
Tensile Creep Modulus, 1000 hours 3300 MPa

@Strain <=0.500 %
 479000 psi

@Strain <=0.500 %
 ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 5.50 µm/m-°C

@Temperature 23.0 - 80.0 °C
 3.06 µin/in-°F

@Temperature 73.4 - 176 °F
 DIN 53752
Specific Heat Capacity 1.50 J/g-°C
0.359 BTU/lb-°F
IEC 1006
Thermal Conductivity 0.270 W/m-K
1.87 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 - 225 °C
428 - 437 °F
DSC; ISO 11357-3
Maximum Service Temperature, Air 110 °C
230 °F
at 50% loss of tensile strength after 20000h; IEC 216-1
140 °C
284 °F
at 50% loss of tensile strength after 5000h; IEC 216-1
170 °C
338 °F
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
ISO 75-2
Decomposition Temperature >= 300 °C
>= 572 °F
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Diameter 0.800 mm
 HB

@Diameter 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+15 ohm-cm
2.00e+15 ohm-cm
IEC 93
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 93
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
 3.4

@Frequency 1.00e+6 Hz
 IEC 250
3.6

@Frequency 100 Hz
 3.6

@Frequency 100 Hz
 IEC 250
Dielectric Strength 117 kV/mm
2970 kV/in
IEC 243/1
Dissipation Factor 0.0030

@Frequency 100 Hz
 0.0030

@Frequency 100 Hz
 IEC 250
0.021

@Frequency 1.00e+6 Hz
 0.021

@Frequency 1.00e+6 Hz
 IEC 250
Comparative Tracking Index 125 V
125 V
Test solution B; IEC 112
375 V
375 V
Test solution A; IEC 112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 260 °C
500 °F
Feeding zone
Zone 2 265 °C
509 °F
Compression
Zone 3 270 °C
518 °F
Metering-zone
Zone 4 270 °C
518 °F
Nozzle
Melt Temperature 250 - 275 °C
482 - 527 °F
Injection-molding
270 °C
518 °F
for shrinkage test, Optimal
Mold Temperature 60.0 - 100 °C
140 - 212 °F
80.0 °C
176 °F
for shrinkage test, Optimal
Drying Temperature 80.0 - 120 °C
176 - 248 °F
Dry Time 4 hour
4 hour
Descriptive Properties Value Comments
Color Natural, Colored and Black
Commercial Status Europe
Ignition Temperature >400°C
ASTM D1929
Peripheral screw speed < 0.25 m/s
Primary Processing Technique Injection Molding