- PolyOne Stat-Tech™ AT-CB2/000 CR Acetal (POM) Copolymer
PolyOne Stat-Tech™ AT-CB2/000 CR Acetal (POM) Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | PolyOne Corporation |
| Trade Name | Stat-Tech™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ AT-CB2/000 CR Acetal (POM) Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Stat-Tech™ AT-CB2/000 CR XP020229R2Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 - 1.42 g/cc | 1.36 - 1.42 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.025 - 0.028 cm/cm | 0.025 - 0.028 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.7 - 68.9 MPa | 7500 - 9990 psi | ASTM D638 |
| Elongation at Break | 10 - 20 % | 10 - 20 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.07 - 4.14 GPa | 300 - 600 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 82.7 - 103 MPa | 12000 - 14900 psi | ASTM D790 |
| Flexural Modulus | 1.38 - 3.45 GPa | 200 - 500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 - 1.30 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.993 - 2.44 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C @Thickness 3.18 mm |
307 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C @Thickness 3.18 mm |
221 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 - 1.00e+7 ohm-cm | 10000 - 1.00e+7 ohm-cm | ASTM D257 |
| Surface Resistance | 1e+05 - 1.00e+8 ohm | 1e+05 - 1.00e+8 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 200 °C | 374 - 392 °F | |
| Mold Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2.00 - 3.00 hour | 2.00 - 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Clean/High Purity | |
| Filler / Reinforcement | Carbon Nano Filler | |
| Forms | Pellets | |
| Generic Material | Acetal (POM) Copolymer | |
| Generic Name | Acetal (POM) Copolymer | |
| Processing Method | Injection Molding | |
| Regional Availability | Asia Pacific | |
| Uses | Aerospace Applications | |
| Automotive Electronics | ||
| Business Equipment | ||
| Computer Components | ||
| Connectors | ||
| Electrical Housing | ||
| Electrical/Electronic Applications | ||
| Housings |
Users viewing this material also viewed the following:
- Proto3000 Objet Digital Materials™ DM_8330 Rigid Opaque Prototyping Polymer
- Polymer Resources PC/ABS-FR1-[color]-WR Flame Retardant PC/ABS Alloy, Wear Resistant
- Plastcom SLOVAMID 6 HI-M PA6 with improved impact strength
- Indium Corp. Indalloy 194 Gold Solder Alloy
- SABIC Innovative Plastics ULTEM 2410 PEI (Europe-Africa-Middle East)
- Hexcel® HexForce™ AGP370-5H Carbon Fabric
- Eurostar Staramide 6 80E10 PA6, Injection Molded
- E-Polymers TEKANATE® G7010FR General Purpose Flame Retardant Polycarbonate
- BASF Neopolen® P 9435 0.05 g/cc Core density; Expanded Polypropylene (Europe)
- Lubrizol ESTANE® 58315 Ether Based Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved