SABIC Innovative Plastics LNP FARADEX NS003 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP FARADEX
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP FARADEX NS003 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* FARADEX* NS003 is a compound based on PC+ABS resin containing 15% Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding.
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
ISO 1183
1.24 g/cc
0.0448 lb/in³
ASTM D792
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Time 86400 sec
 0.0030 in/in

@Time 24.0 hour
 ASTM D955
0.0030 cm/cm

@Time 86400 sec
 0.0030 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0035 cm/cm

@Time 86400 sec
 0.0035 in/in

@Time 24.0 hour
 ASTM D955
0.0035 cm/cm

@Time 86400 sec
 0.0035 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
ISO 527
49.0 MPa
7110 psi
ASTM D638
Tensile Strength, Yield 50.0 MPa
7250 psi
ISO 527
52.0 MPa
7540 psi
ASTM D638
Elongation at Break 4.7 %
4.7 %
ASTM D638
6.0 %
6.0 %
ISO 527
Elongation at Yield 3.3 %
3.3 %
ASTM D638
3.5 %
3.5 %
ISO 527
Tensile Modulus 2.70 GPa
392 ksi
1 mm/min; ISO 527
3.10 GPa
450 ksi
50 mm/min; ASTM D638
Flexural Strength 86.0 MPa
12500 psi
ISO 178
89.0 MPa
12900 psi
ASTM D790
Flexural Modulus 2.80 GPa
406 ksi
ISO 178
2.99 GPa
434 ksi
ASTM D790
Izod Impact, Notched 0.740 J/cm
1.39 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.73 J/cm
10.7 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 32.0 kJ/m²
15.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 15.0 J
11.1 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 59.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 32.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
77.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 43.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 35.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
82.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 45.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 115 °C
239 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
120 °C

@Thickness 3.20 mm
 248 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 103 °C
217 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
105 °C

@Thickness 3.20 mm
 221 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 10000 ohm-cm
10000 ohm-cm
ASTM D257
Surface Resistance 10 - 1000 ohm
10 - 1000 ohm
ASTM D257
Shielding Effectiveness 50 - 65 dB

@Thickness 3.00 mm
 50 - 65 dB

@Thickness 0.118 in
 SABIC Method