- Styron Pulse® A35-105 PC/ABS
Styron Pulse® A35-105 PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® A35-105 PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PULSEâ„¢ A35-105 engineering resins give exceptional impact strength even at low temperatures and have high heat distortion temperature.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO R1183 B |
| Water Absorption | 0.20 - 0.60 % | 0.20 - 0.60 % | ISO R 62 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ISO 1133 |
| 12 g/10 min @Load 5.00 kg, Temperature 250 °C |
12 g/10 min @Load 11.0 lb, Temperature 482 °F |
ISO 1133 | |
| 17 g/10 min @Load 5.00 kg, Temperature 260 °C |
17 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 105 MPa | 15200 psi | DIN 53459 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO R 527 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ISO R 527 |
| Elongation at Break | >= 80 % | >= 80 % | ISO R 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO R 527 |
| Flexural Strength | 82.0 MPa | 11900 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 3 points; ISO 178 |
| Izod Impact, Notched (ISO) | 50.0 kJ/m² @Temperature -40.0 °C |
23.8 ft-lb/in² @Temperature -40.0 °F |
ISO R 180 |
| 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO R 180 | |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -40.0 °C |
9.52 ft-lb/in² @Temperature -40.0 °F |
ISO R179 |
| 2.80 J/cm² @Temperature 0.000 °C |
13.3 ft-lb/in² @Temperature 32.0 °F |
ISO R179 | |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO R179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 - 80.0 µm/m-°C @Temperature 0.000 - 80.0 °C |
41.7 - 44.4 µin/in-°F @Temperature 32.0 - 176 °F |
ASTM D696 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 126 °C | 259 °F | unannealed; ISO 75 B |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | unannealed; ISO 75 A |
| Vicat Softening Point | 122 °C | 252 °F | 50°C/hr, 5 kg; ISO 306 B |
| 142 °C | 288 °F | 120°C/hr, 1 kg; ISO 306 A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Oxygen Index | 20 % | 20 % | ASTM D2863 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F |
Users viewing this material also viewed the following:
- Lucite International Perspexâ„¢ XT Acrylic Extruded Sheet 0X00
- Gouda Vuurvast VIBRON 160 K 50 Dense Vibrating Refractory Castable
- SABIC Innovative Plastics ULTEM HU1100 PEI (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP PF008 PA 6 (Asia Pacific)
- Loctite® 3951 Gap filling, flexible Urethane Adhesive
- DuPont Performance Polymers Minlon® 11C140 BK086 Nylon 66 (Unverified Data**)
- Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1150M (Heated 760°C/2hr/AC then 621°C/4hr/AC)
- Addiplast Addinyl B2 G30 Nylon 6, 30% Glass Bead
- Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved