- Polyvinylidinefluoride (PVDF), Molded/Extruded
- Manifattura Cattaneo PVDF
Manifattura Cattaneo PVDF
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo PVDF.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.79 g/cc | 0.0647 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.050 % @Temperature 23.0 °C |
0.050 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 0.050 % | 0.050 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 75 | 75 | ISO 2039-2 |
| Tensile Strength at Break | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527 |
| Tensile Strength, Yield | 50.0 - 55.0 MPa | 7250 - 7980 psi | ISO 527 |
| Elongation at Break | 20 - 60 % | 20 - 60 % | ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527 |
| Flexural Strength | 74.0 MPa | 10700 psi | |
| Flexural Modulus | 2.25 GPa | 326 ksi | ISO 178 |
| Compressive Yield Strength | 17.0 MPa @Strain 1.00 % |
2470 psi @Strain 1.00 % |
ISO 604 |
| Poissons Ratio | 0.35 | 0.35 | |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 |
| Coefficient of Friction, Dynamic | 0.20 - 0.35 | 0.20 - 0.35 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | on polished steel; MPC Test |
| K Factor (Wear Factor) | 0.60 | 0.60 | µm/s. PV = 0.1 MPa-m/s; max P = 25 MPa; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 125 - 140 µm/m-°C @Temperature 23.0 - 100 °C |
69.4 - 77.8 µin/in-°F @Temperature 73.4 - 212 °F |
ASTM D696 |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | DOM 52612 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 44 % | 44 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+16 ohm-cm | 5.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60094 |
| Dielectric Constant | 7.5 @Frequency 1.00e+6 Hz |
7.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 20.0 - 30.0 kV/mm @Thickness 2.00 mm |
508 - 762 kV/in @Thickness 0.0787 in |
IEC 60243 |
| Dielectric Loss Index | 0.15 @Frequency 1.00e+6 Hz |
0.15 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | Yes | Yes |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White | |
| UV Resistance | Y |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® FC 20 Low Density Polyethylene - Blown Film Extrusion
- Pacific Sintered Materials FN-255-S Nickel Steel Powdered Metal
- Loxim 500 00V0 Polycarbonate/Acrylonitrile Butadiene Styrene
- Momentive Performance Materials RTV157 High Strength Silicone Adhesive Sealant, Gray
- Lucent Polymers TPO-30T Thermoplastic Polyolefin, 30% Mineral Filled
- Tipco Tipcolene® CR 8229 - 20% Talc/Mineral Reinforced Polypropylene Copolymer Compound with Controlled Rheology
- Hexcel® Redux® 335U Adhesive film for bonding metallic and composite components (0.03 psf)
- EMS-Grivory Grivory® XE 3959 black 9992 PA610
Copyright © lookpolymers.com All Rights Reserved