SABIC Innovative Plastics LNP THERMOCOMP NX07354 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP NX07354 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This is a PC/ABS compound, a good candidate for Laser Direct Structuring applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0074 cm/cm | 0.0074 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0063 cm/cm | 0.0063 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.0 MPa | 6090 psi | 5 mm/min; ISO 527 |
| 43.0 MPa | 6240 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D638 |
| 53.0 MPa | 7690 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 7.4 % | 7.4 % | Flexural Strain, break, 2 mm/min; ISO 178 |
| 40 % | 40 % | 5 mm/min; ISO 527 | |
| 42.3 % | 42.3 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.6 % | 4.6 % | 5 mm/min; ISO 527 |
| 4.7 % | 4.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| 2.34 GPa | 339 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.24 GPa | 325 ksi | 2 mm/min; ISO 178 |
| 2.31 GPa | 335 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 6.06 J/cm | 11.4 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 54.0 kJ/m² | 25.7 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 84.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.74 @Frequency 1.00e+9 Hz |
2.74 @Frequency 1.00e+9 Hz |
ASTM D150 |
| Dissipation Factor | 0.0030 @Frequency 1.00e+9 Hz |
0.0030 @Frequency 1.00e+9 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- NCMT NanoPAC™ G1000 High Performance Polypropylene Nanocomposite
- Premix Thermoplastics PRE-ELEC® PP 1399 Dissipative Thermoplastic Compound
- Polymer Resources PC/TP-GP2 PC Polyester, High Impact, Excellent Chemical Resistance (Unverified Data**)&
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 63A
- Global BM-3245-PC High Density Polyethylene, Pipe Extrusion Grade
- Silberline StarBrite® 2100
- Universal Wire Works AM355 (AMS 5780) Filler Metal
- Wanhua Chemical Wanthane® WHT-1195 Polyester Based TPU
Copyright © lookpolymers.com All Rights Reserved