- SABIC Innovative Plastics Xenoy® X5410 PC+PET (Europe-Africa-Middle East)
SABIC Innovative Plastics Xenoy® X5410 PC+PET (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® X5410 PC+PET (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mineral filled PC+PET resin with high heat dimensional stability for paint systems. It has very low CTE and excellent flow - impact balance for automotive exterior applications, like body panels, tailgates, spoilers, rockerpanels or tankflaps
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.140 % | 0.140 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.42 % | 0.42 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0065 - 0.0075 cm/cm @Thickness 3.20 mm |
0.0065 - 0.0075 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 250 °C |
0.20 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| 19 g/10 min @Load 2.16 kg, Temperature 265 °C |
19 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 | |
| Melt Index of Compound | 17 g/10 min @Load 2.16 kg, Temperature 265 °C |
17 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 26.0 MPa | 3770 psi | 5 mm/min; ISO 527 |
| 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D638 | |
| 45.0 MPa | 6530 psi | Type I, 10 mm/min; SABIC - Japan Method | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 | |
| 56.0 MPa | 8120 psi | Type I, 10 mm/min; SABIC - Japan Method | |
| Elongation at Break | 12.1 % | 12.1 % | 5 mm/min; ISO 527 |
| 38.7 % | 38.7 % | Type I, 5 mm/min; ASTM D638 | |
| 100 % | 100 % | Type I, 10 mm/min; SABIC - Japan Method | |
| Elongation at Yield | 4.1 % | 4.1 % | 5 mm/min; ISO 527 |
| 4.2 % | 4.2 % | Type I, 5 mm/min; ASTM D638 | |
| 67 % | 67 % | Type I, 10 mm/min; SABIC - Japan Method | |
| Tensile Modulus | 3.19 GPa | 463 ksi | 1 mm/min; ISO 527 |
| 3.23 GPa | 468 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 93.0 MPa | 13500 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.70 GPa | 392 ksi | 2 mm/min; ISO 178 |
| 2.99 GPa | 434 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.870 J/cm | 1.63 ft-lb/in | ASTM D256 |
| 0.820 J/cm @Temperature -30.0 °C |
1.54 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 54.0 J @Temperature 23.0 °C |
39.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 58.1 µm/m-°C @Temperature -30.0 - 80.0 °C |
32.3 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 |
| 58.6 µm/m-°C @Temperature -40.0 - 60.0 °C |
32.6 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 70.1 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| 70.5 µm/m-°C @Temperature -40.0 - 60.0 °C |
39.2 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 134 °C @Thickness 6.40 mm |
273 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 109 °C @Thickness 3.20 mm |
228 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 121 °C @Thickness 6.40 mm |
250 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 137 °C | 279 °F | Rate B/50; ASTM D1525 |
| 137 °C | 279 °F | Rate B/50; ISO 306 | |
| 140 °C | 284 °F | Rate B/120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | Pass | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Old Hickory 54-S Kentucky Ball Clay
- Premix Thermoplastics PRE-ELEC® PP 1397 Conductive Thermoplastic Compound
- Dielectric Polymers NT-240APS High Temperature Laminating Adhesive (discontinued **)
- Kingfa FRABS-518 Flame Retardant ABS
- Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire
- Lehmann & Voss LUVOCOM® 1105-0918/BL PEEK, with glass fiber
- SABIC Innovative Plastics LNP STAT-KON TD000 PU
- Teknor Apex APEX® 65290 Polyvinyl Chloride, Flexible
- A. Schulman POLYBATCH™ Bright White P80514PF Concentrate Based In Polypropylene
- Polyram RamLloy PN300G6 PPE/PS Alloy, 30% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved