- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 94.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 94.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C @Thickness 3.20 mm |
201 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® C2951 PC+ABS (Asia Pacific) CYCOLOY C2951 is a flame retardant PC+ABS free from chlorinated or brominated flame retardant additives. High heat resistance is offered for demanding electrical applications, whilst maintaining exc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP FARADEX NX96302 PC+ABS LNP* FARADEX* NX96302 is a compound based on PC+ABS resin containing Stainless Steel Fibers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | |
| Ineos ABS Lustran® QE 1045 A, Injection Grade
(discontinued **) Injection molding grade, high modulus, only available in black.Applications: For automotive application.Information provided by Bayer.LANXESS was spun-off from Bayer in early 2005. Business renamed.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | |
| Ineos ABS Lustran® QE 1455/L2, Injection Grade
(discontinued **) Injection molding grade, increased heat resistance, medium gloss, UV-stabilized grade.Applications: Automotive: body parts.Information provided by Bayer.LANXESS was spun-off from Bayer in early 2005.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Gichem GILAC G160 Acrylonitrile Butadiene Styrene
(discontinued **) ABS very high fluidity, good resilience. Medium-High Injection speed.Information provided by GICHEM Gruppo Industriale Chimico |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| LG Chemical LUPOS GP-2201F General Purpose ABS, 20% Glass Fiber Reinforced, Flame Retardant LUPOS resins are glass fiber reinforced styrene copolymers. LUPOS have improved strength, rigidity and dimensional stability. They offer excellent heat resistance, minimal mold shrinkage and have .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | 80x10x4mm; ISO 75-2/Af |
| SYNTHOS Forsan® 449 Acrylonitrile Butadiene Styrene (ABS) High flow, high gloss, suitable for electroplating.Applications: General purpose, intricate and thin-walled productsHousehold appliances, vacuum cleaners, heels, toys, fan grilles, etc.Synthos was f.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRILOY D20001 PC (Asia Pacific) LNP LUBRILOY* D20001 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Xenoy® IQ4840 PBT+PC (Asia Pacific) Xenoy iQ4840 (PBT+PC) resin is an environmental responsible, sustainable, and low carbon footprint resin. It is a 10% mineral filled resin with high modulus and ductile (HMD) characteristics. Xen.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Xenoy® X4820 PBT+PC (Europe-Africa-Middle East) Xenoy X4820 is a high modulus PC/PBT Blend. This resin provides high chemical resistance, excellent impact, very low creep, low CTE, excellent fatigue and dimensional stability. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C @Thickness 3.20 mm |
201 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP 67002XXH PBT+PC LNP* THERMOCOMP* 67002XXH is a compound based on PBT+PC containing proprietary antimicrobial additives. Designed for touch surfaces in patient critical healthcare applications. Added features inc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP WBL36L PBT LNP* LUBRICOMP* WBL36L is a compound based on PBT resin containing 30% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Styrolution NAS® 36 UV Stabilized Acrylic Copolymer Features:Sparkling clarity Excellent indoor light stability Styrenic processing advantages Scratch resistant Enhanced mold releaseApplications:Appliances Point-of -Purchase Displays Toys Office Acce.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | 0.5 inch unannealed; ASTM D648 |
| PlastxWorld CEVIAN® SERG1 10% GF ABS Glass fiber reinforced and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 127UVE RD402 Acetal (POM)
(Unverified Data**) UV Stabilized High Viscosity Acetal Homopolymer with Very Low Emissions Delrin 127UVE RD402 (formerly DE20555) is a high viscosity acetal homopolymer with UV stabilizers pigmented red with very low .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 527UVE RD402 Acetal (POM)
(Unverified Data**) UV Stabilized Medium Viscosity Acetal Homopolymer with Very Low Emissions Delrin 527UVE RD402 (formerly DE20556) is a medium viscosity acetal homopolymer with UV stabilizers pigmented red with very .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | annealed; ISO 75 |
| Chi Mei Polyrex® PH-88S Polystyrene - Extrusion Extrusion |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Starflam P10003 PA6, Mineral Filled, Flame Retardant, Extrusion Starflam P10003 is a Mineral Filled, Halogen Free, Red Phosphorous Free, Flame Retardant, Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | annealed; ISO 75 |
| Chi Mei Polyrex® PG-80 Polystyrene High strength |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron AP-78 EP ABS Electro Plating Applications Electroplating & Hot Stamping GradesInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron IM-11 ABS Injection Molding Grade High Impact, High Rigidity, High Fatigue, Low Flow, PaintableInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron IM-29 ABS Injection Molding Grade High Impact, Medium, High Flow, General PurposeInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron SE-22M ABS Sheet Extrusion Grade Sheet Extrusion grade for profile & DoorsInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C @Thickness 6.40 mm |
201 °F @Thickness 0.252 in |
Method A; ASTM D648 |
| Bhansali Engineering Abstron SE45I Extrusion ABS Very High Impact, Low Flow, High Rigidity and Sheet/Pipe/Profile applicationInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron HI-40 ABS High Impact Injection Molding Very High & Medium Impact, Paintable Automotive Grades Information provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Styrolution NAS® 21 Acrylic Copolymer Features:Sparkling clarity Scratch resistant Can be blended with K-Resin at any level to modify flexibility, surface hardness, heat distortion temperatures, etc. Styrenic processing advantages Gamma.. |
|||