Chi Mei Polylac® PA-737 ABS - High Flow
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-737 ABS - High Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow, medium impact
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 33 g/10 min @Load 10.0 kg, Temperature 220 °C |
33 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO-1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Ball Indentation Hardness | 94.0 MPa | 13600 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; ISO 527 |
| Flexural Strength | 60.0 MPa | 8700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 2.33 J/cm @Thickness 6.35 mm |
4.37 ft-lb/in @Thickness 0.250 in |
|
| 2.55 J/cm @Thickness 3.17 mm |
4.78 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 2.10 J/cm² | 9.99 ft-lb/in² | ISO 179 |
| Impact | 16.0 | 16.0 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | unannealed; ISO 75 |
| 94.0 °C | 201 °F | annealed; ISO 75 | |
| Vicat Softening Point | 93.0 °C @Load 5.00 kg |
199 °F @Load 11.0 lb |
120°C/hr; ISO 306 |
| 94.0 °C @Load 5.00 kg |
201 °F @Load 11.0 lb |
50°C/hr; ISO 306 | |
| 99.0 °C @Load 1.00 kg |
210 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 101 °C @Load 1.00 kg |
214 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® HS 630 HSR Emulsion Resin - Rubber Masterbatch
- Owens Corning Glass Fiber Reinforced Polyester BMC (Injection), 22 wt.% glass
- H.C. Starck Amperweld® 1701.39 K1 Chromium Carbide RIII
- Taiwan Sheen Soon Sheenthane® A8210F Thermoplastic Polyurethane Elastomer
- STAR Thermoplastic Alloys & Rubbers StarTUFF TF 40-LR-9 TPE
- Master Bond Supreme 3HT High Bond Strength One Component Epoxy Adhesive System
- Formosa Plastics Formolon® 40 PVC
- DuPont Teijin Films Teijin® Tetoron® G2 Polyester Film, 75 Gauge
- Addcomp ADD-VANCE® DS 785 Desiccant masterbatch in PP carrier
Copyright © lookpolymers.com All Rights Reserved