Gichem GILAC G160 Acrylonitrile Butadiene Styrene (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gichem GILAC G160 Acrylonitrile Butadiene Styrene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS very high fluidity, good resilience. Medium-High Injection speed.Information provided by GICHEM Gruppo Industriale Chimico
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 35 g/10 min | 35 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Yield | 25 % | 25 % | ASTM D638 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| 1.00 J/cm @Temperature 0.000 °C |
1.87 ft-lb/in @Temperature 32.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525/A |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
|
| Flammability Test | 75 | 75 | [°C] Bilia; IEC 331 |
| Oxygen Index | 19 % | 19 % | ASTM D2863 |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 220 °C | 428 °F | |
| Mold Temperature | 50.0 - 60.0 °C | 122 - 140 °F | |
| Drying Temperature | 80.0 °C | 176 °F | 2 hours |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1700-7910 PPO, with carbon fiber
- SABIC Innovative Plastics LNP LUBRICOMP OFL36 PPS - Linear
- A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade
- Hexcel® HexForce™ 3780 Fiber Glass Fabric
- Borealis Nepol™ GB601HP Polypropylene, 30% Long Glass Fiber Reinforced w/HK060AE
- Elmer's Products Aron Alpha® 221F Cyanoacrylate Adhesive (Industrial Krazy Glue™)
- Arlon 0.020" (0.508 mm) Flexible Heater Silicone with Fiberglass Substrate (51586R020)
- BASF Novolen® 2448 L Polypropylene
- PolyOne Lubri-Tech™ SF-000/40T Polyphenylene Sulfide - 40% PTFE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved