- Chi Mei Polyrex® PG-80 Polystyrene
Chi Mei Polyrex® PG-80 Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polyrex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polyrex® PG-80 Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High strength
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Melt Flow | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 144 MPa | 20900 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Flexural Strength | 68.0 MPa | 9860 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | ISO 180/1C |
| Charpy Impact Unnotched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 |
| Impact | 3.00 | 3.00 | Impact Flexural Test Notched (KJ/m²) |
| 17.0 | 17.0 | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | unannealed; ISO 75 |
| 94.0 °C | 201 °F | annealed; ISO 75 | |
| Vicat Softening Point | 94.0 °C @Load 5.00 kg |
201 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 96.0 °C @Load 1.00 kg |
205 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 97.0 °C @Load 5.00 kg |
207 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 102 °C @Load 1.00 kg |
216 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CP - 71 LL General Purpose Acrylic Resin
- Malvern Minerals Novakup® 325 Surface-Treated Lamellar Quartz Filler/Extender
- Freudenberg Simrit Hydrolysis-Resistant Polyurethane Elastomer
- Stir SpA B 3060 AT (PVC)
- SABIC Innovative Plastics LNP Thermocomp WH0500B PBT (Asia Pacific)
- Chase Plastics CP Pryme® N100L (DAM) Nylon 6, Internally Lubricated
- Denka LCS Z1075 Thermoplastic Elastomer, Extrusion grade (general)
- Clariant Renol PP1100G40 Polypropylene Homopolymer, 40% Glass Fiber, Chemically Coupled
- BNZ Materials Bazelite 2300 LI Insulating Castable
- Polimeri Europa KOBLEND PCA 839 PC+ABS (discontinued **)
Copyright © lookpolymers.com All Rights Reserved