Ineos ABS Lustran® M205FC ABS Pellets, Injection Molding Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Ineos ABS
Trade Name Lustran®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® M205FC ABS Pellets, Injection Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Injection Molding grade for medical applications (e.g. inhalers, roller clamps, spikes, etc.)/ Biocompatible with up to 30 days human contact duration according to USP Class VI and ISO 10993-1. Food contact acc. to BfR and FDA, DMF registered. Good flowing, standard impact strength
Physical Properties Metric English Comments
Density 1.055 g/cc
0.03811 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
Test Condition: 150x105x3; 500 bar; acc. ISO 2577
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
Test Condition: 150x105x3; 500 bar; acc. ISO 2577
Melt Flow 20 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 20 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 106 MPa
15400 psi
ISO 2039-1
Tensile Strength at Break 36.5 MPa
5290 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 50.5 MPa
7320 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 15 %
>= 15 %
50 mm/min; acc. ISO 527-1,-2
20 %
20 %
50 mm/min, Nominal; ISO 527-1,-2
Elongation at Yield 2.6 %
2.6 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.55 GPa
370 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 75.0 MPa
10900 psi
2 mm/min; ISO 178
Flexural Modulus 2.60 GPa
377 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
15.0 kJ/m²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
Charpy Impact Unnotched 10.0 J/cm²

@Temperature -30.0 °C
 47.6 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
12.4 J/cm²

@Temperature 23.0 °C
 59.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
1.60 J/cm²

@Temperature 23.0 °C
 7.61 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear 78.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 43.3 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2; Parallel to Flow
CTE, linear, Transverse to Flow 81.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 45.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi) 98.0 °C
208 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 94.0 °C
201 °F
ISO 75-1,-2
Vicat Softening Point 98.0 °C

@Load 5.10 kg
 208 °F

@Load 11.2 lb
 50°C/hour; ISO 306
101 °C

@Load 5.10 kg
 214 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+16 ohm-cm
2.00e+16 ohm-cm
IEC 60093
Surface Resistance 2.00e+17 ohm
2.00e+17 ohm
IEC 60093
Dielectric Constant 2.82

@Frequency 1.00e+6 Hz
 2.82

@Frequency 1.00e+6 Hz
 IEC 60250
3.04

@Frequency 100 Hz
 3.04

@Frequency 100 Hz
 IEC 60250
Dissipation Factor 0.0053

@Frequency 100 Hz
 0.0053

@Frequency 100 Hz
 IEC 60250
0.0096

@Frequency 1.00e+6 Hz
 0.0096

@Frequency 1.00e+6 Hz
 IEC 60250
Processing Properties Metric English Comments
Melt Temperature 240 °C
464 °F
Injection Molding; ISO 294
Mold Temperature 70.0 °C
158 °F
Injection Molding; ISO 294
Injection Velocity 240 mm/sec
9.45 in/sec
Injection Molding; ISO 294