- Acrylonitrile Butadiene Styrene (ABS), Molded
- Ineos ABS Lustran® E401
Ineos ABS Lustran® E401
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® E401.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Very high surface resistance, high surface gloss.,Property data per ISO test methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
Estimated using room temperature density |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | |
| Elongation at Yield | 2.5 % | 2.5 % | |
| Tensile Modulus | 1.90 GPa | 276 ksi | |
| Charpy Impact Unnotched | 21.0 J/cm² | 99.9 ft-lb/in² | |
| 17.0 J/cm² @Temperature -30.0 °C |
80.9 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | |
| 1.60 J/cm² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 0.900 µm/m-°C @Temperature 20.0 °C |
0.500 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | |
| Vicat Softening Point | 99.0 °C | 210 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
|
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
|
| 0.0090 @Frequency 1e+6 Hz |
0.0090 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- LATI Latilub 57-10T Y/15 PPA, Aramid Reinforced
- Solvay Specialty Polymers Radel® R-7159 Polyphenylsulfone (PPSU)
- Sumitomo Chemical ESPOLEX® UT412A Thermoplastic Elastomer
- ThyssenKrupp 51CrV4 Saw Steel, Hot-Rolled Strip
- Trelleborg Neoprene® C739 Chloroprene
- A. Schulman POLYTROPE™ TPP 620 Olefinic Elastomer
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 0.75 PHR Zinc Stearate
- Dow Corning SYL-OFF® PMCPSL 9176 Anchorage Additive
- BASF Elastollan® C-60AW Polyester Type Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved