SABIC Innovative Plastics LNP STAT-KON MX01739C PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON MX01739C PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* SAT-KON* MX01739C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 |
| 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm @Time 86400 sec |
0.0060 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.040 cm/cm @Time 86400 sec |
0.010 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 5 mm/min; ISO 527 |
| 28.0 MPa | 4060 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 0.80 % | 0.80 % | Type I, 5 mm/min; ASTM D638 |
| 0.90 % | 0.90 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 5.24 GPa | 760 ksi | 1 mm/min; ISO 527 |
| 6.93 GPa | 1010 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| Flexural Yield Strength | 41.0 MPa | 5950 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.58 GPa | 809 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.59 GPa | 811 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.340 J/cm | 0.637 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.680 J/cm | 1.27 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
9.44 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 77.4 µm/m-°C @Temperature -30.0 - 30.0 °C |
43.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 134 °C @Thickness 3.20 mm |
273 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 94.0 °C @Thickness 3.20 mm |
201 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 4.0 - 7.0 ohm | 4.0 - 7.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-30-20 Supported Urethane Foam, Very Soft, Supported with Clear Polyester Film
- Nilit FRIANYL B63 D-S 5 Nylon 6., std. viscosity for injection molding
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Raw Polymer
- BP Amoco Acctuf® 3045 Impact Copolymer Polypropylene (discontinued **)
- Chevron Phillips Marlex® KN 226 LDPE Injection Molding Resin
- DuPont Performance Polymers Zytel® HTN 92G45DH2 BK083 Polyphthalamide (PPA)
- ACC EP RSP EPI Engineered Polymers Silicone Polyurea
- DSM Arnitel® UM551 55 Shore D Copolyester Elastomer (North America)