SABIC Innovative Plastics LNP Thermocomp RX06324 PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp RX06324 PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This material is Mineral filled Nylon grade with high dielectric constantThis data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.19 g/cc | 0.0791 lb/in³ | ASTM D 792 |
| 2.19 g/cc | 0.0791 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 2.0 % @Time 86400 sec |
2.0 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0128 cm/cm @Time 86400 sec |
0.0128 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0108 cm/cm @Time 86400 sec |
0.0108 in/in @Time 24.0 hour |
ASTM D 955 |
| Melt Flow | 17 g/10 min @Load 1.20 kg, Temperature 270 °C |
17 g/10 min @Load 2.65 lb, Temperature 518 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D 638 |
| 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 5.12 GPa | 743 ksi | 50 mm/min; ASTM D 638 |
| 5.23 GPa | 759 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Yield Strength | 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 4.44 GPa | 644 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 5.01 GPa | 727 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm @Temperature 23.0 °C |
0.693 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.52 J/cm @Temperature 23.0 °C |
6.59 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² @Temperature 23.0 °C |
10.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 7.9 @Frequency 9.00e+8 Hz |
7.9 @Frequency 9.00e+8 Hz |
ASTM D 2520 - Mth B |
| Dissipation Factor | 0.011 @Frequency 9.00e+8 Hz |
0.011 @Frequency 9.00e+8 Hz |
ASTM D 150 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JD455CJ Polyvinyl Chloride, Flexible (PVC, Flexible)
- Parker Chomerics METALASTIC® Gasketing Wire Mesh EMI Gasket Selection Guide
- Kennametal Stellite Deloro® 75 Nickel Alloy
- LG Chemical LUPOL HI5204B PP+MF20%
- LATI Latiohm 63-08 PD02 G/25 PA6, 25% Glass Fiber Reinforced
- SABIC Innovative Plastics LNP THERMOCOMP MF006SXP PP (Europe-Africa-Middle East)
- Techmer ES HiFill® PA4/6 GF5 IM HS BK 5% Glass Filled
- Axion Polymers Axpoly® HDPE21 1000 High Purity Molding
- 3M S38 Glass Bubbles
- Aremco AREMCOLOX™ 502-676 Machinable Magnesium Oxide
Copyright © lookpolymers.com All Rights Reserved