Ineos ABS Lustran® M203FC
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® M203FC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Standard impact strength, easy flowing, high gloss, BgVV and FDA quality for food contact. ,Property data per ISO test methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 33 g/10 min @Load 10.0 kg, Temperature 220 °C |
33 g/10 min @Load 22.0 lb, Temperature 428 °F |
Estimated using room temperature density |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | |
| Elongation at Yield | 2.6 % | 2.6 % | |
| Tensile Modulus | 2.40 GPa | 348 ksi | |
| Charpy Impact Unnotched | 11.0 J/cm² | 52.4 ft-lb/in² | |
| 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 0.900 µm/m-°C @Temperature 20.0 °C |
0.500 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | |
| Vicat Softening Point | 99.0 °C | 210 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
|
| 3.0 @Frequency 100 Hz |
3.0 @Frequency 100 Hz |
||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
|
| 0.0090 @Frequency 1e+6 Hz |
0.0090 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Meilian Chemical W9350 WHITE MASTERBATCH
- Multibase Multi-Flex® A 7202 MR TPE Thermoplastic Elastomer
- Saint-Gobain CHR® SG36-03(R) Industrial Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- PlastxWorld CEVIAN®-V 500 ABS
- Covestro Bayblend® R-FR610 Polycarbonate Recyclate Blend
- ChevronTexaco Texglass MV
- DuPont Performance Polymers Crastin® FG6129 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)<
- Ensinger Hydel® PC-7 Polycarbonate (PC)
- Azdel SuperLite® SL551600-100 PP Resin Matrix / 55% Glass Fiber (5 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved