LG Chemical NT-520 ABS, High Flow, Non Toxic
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical NT-520 ABS, High Flow, Non Toxic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ISO 2577 |
| Melt Index of Compound | 42 g/10 min @Load 10.0 kg, Temperature 220 °C |
42 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 12 % | 12 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 67.0 MPa | 9720 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 80 | |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C |
40.5 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 2.60 J/cm² @Temperature 23.0 °C |
12.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 95.0 µm/m-°C @Temperature 20.0 °C |
52.8 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 93.0 µm/m-°C @Temperature 20.0 °C |
51.7 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | Annealed, 80°C, 4 hours; ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Annealed, 80°C, 4 hours; ISO 175 |
| Vicat Softening Point | 96.0 °C | 205 °F | 50 N, 50°C/h; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 GV15 Nylon 6.6 for injection molding, 15% glass fiber reinforced
- SABIC Innovative Plastics Xenoy® 1760 PBT+PC (Asia Pacific)
- Polyplastics TOPAS® 6013 Cyclic Olefin Copolymer (COC) (Asia/Pacific Grade)
- Tipco Tipcolite® TG 311 Phenolic Compound, Mineral & Wood Flour, Medium Flow & High Electrical Properties
- Wieland 1007 Wilaform Gold
- Cossa Polimeri ESTADIENE 1016 V0 Flame Retardant ABS
- Chosun Refractories A18S Magnesia Carbon Bricks for Electric Arc Furnace
- Clariant Renol PA111BK S&P Nylon 66, General Purpose
- Fainplast Compounds RKT 736 Rigid PVC, Extrusion Lead Free
Copyright © lookpolymers.com All Rights Reserved