- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 220 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 220 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | |
| Plastcom SLOVAMID 6 GF 7 T 13 PA6, 7% glass fibre, 13% mineral filling FeaturesGood anisotropy of the manufacturing shrinkage. The talc is added to get the material shrinkage identical in both directions. Application for flat products in disc form /no screw after cooli.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | DIN 53461 |
| Qualchem Danamid AFGF-20 Polyamide 66, 20% Glass Fiber Reinforced with glass fiberInformation provided by Qualchem Zrt. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 - 268 °C | 428 - 514 °F | Average value: 250 °C Grade Count:10 |
| Overview of materials for Polyphenylene Sulfide (PPS), Conductive This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Conductive". Each property range of values reported is minimum and maximum .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Lanxess Durethan® AKV 30 GIT H2.0 900116 Nylon 66, 30% Glass Fiber PA 66, injection molding grade, 30% glass fibers, suitable for GIT (gas assisted technology), good surface finish, good heat-ageing resistance |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 220 °C | >= 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP RFL36 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFL36 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP RFN16SXZ PA 66 LNP LUBRICOMP* RFN16SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6/6 GF13 IM-1 HS L 13% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 13% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 220 °C | >= 428 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics LNP STAT-KON RE004 PA 66 (Europe-Africa-Middle East) LNP* Stat-kon* RE004 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON WEF42I PBT LNP* STAT-KON* WEF42I is a compound based on PBT resin containing 10% Carbon Fiber, 20% Glass Fiber. Added features of this grade include: High Impact, Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | |
| Shinil Chemical SHINCON PES Electro Conductive Polymer SHINCON is the product line of SHINIL's electrically conductive compound which is able to dissipate the electrostatic charge (ESD) effectively. Shinil has developed SHINCON products using Shinil's .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | |
| Shinil Chemical SHINFLAME PA-66 GF Flame Retardant Polymer Under Hood SHINFLAME is a flame retardant (FR) compound which exhibits inherent flame retardant properties during fire. Shinil uses its patented dispersion blending technology with variety of polymers to prod.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Shinkong Synthetic Fibers Shinite® T102G30 PET, 30% Glass Filled, Fire Retardant Information from Shinkong Synthetic Fibers Corp. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Unannealed; ASTM D648 |
| Techmer ES Electrablend® PA6/6 03002 CF Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber ReinforcementAdditive: Lubricant, Impact Modifier and Heat StabilizerFeatures: Lubricated, Electrically Conductive, Impact.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Unannealed; ASTM D648 |
| Techmer ES Electrablend® PA6/6 03005 CF Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber ReinforcementAdditive: Lubricant, Impact Modifier and Heat StabilizerFeatures: Lubricated, Electrically Conductive, Impact.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Solvay TECHNYL® 2412GM05-D PA66, 38% glass fiber, DRY Description: Polyamid 66, reinforced with 38% of glass fiber and mineral filler, for injection molding.Available in: Asia PacificProduct Applications: TECHNYL® 2412GM05-D is used in all sectors o.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75 |
| Polyram PlusTek PA823M6 Nylon 6.6 for Injection Molding, 30% Minerals Reinforced, Impact Modified 30% Minerals reinforced, impact modified Nylon 6.6 for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-93 |
| Wellman Wellamid® GF33-66/6 XE-NBK1 33% Glass Fiber Reinforced Nylon 66/6 Description: Glass Fiber Reinforced Nylon 66/6Information provided by Wellman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-93 |
| Wellman Wellamid® MRGF25/25 22H-GY1 Nylon 66, 25% Mineral and 25% Glass Reinforced All information provided by Wellman Engineered Resins. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Toyobo Vylopet® EMC330K Glass Reinforced Polyester, Easy Molding Grade HB UL-94 classApplications: General and high rigidity componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and tracking resistance, c.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 179 |
| CP-Polymer-Technik Wellamid® 6600 MZ 401 CP Combination Nylon 66, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 179 |
| CP-Polymer-Technik Wellamid® 6600/50 GV 15 HWCP 15% Glass Fiber Nylon 66, Impact Modified Until 0°C, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® TSG-50 FA PA666-GF50 Information provided by EMS Grivory |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® TSGZ-50 PA666-GF50 Information provided by EMS Grivory |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75 |
| Eurotec® Tecopet® PT74 GR30 NL XA60 PET, 30% glass fiber reinforced, flame retardant - halogen & red phosphorus free,, heat stabilized, natural Information provided by Eurotec® |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| BASF Ultrason® E 2010 G4 MR SW 15102 20% Glass Filled PESU Information provided by BASF |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 436 Glass/Mineral Reinforced, PBT Alloy Data provided by the manufacturer, ComAlloy International Company.20% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Plenco 50240 PET, Pellet, Injection Molded, Black
(discontinued **) PLENCO 50240 is an engineering grade glass reinforced UL flame rated polyethylene terephthalate resin designed for excellent dimensional stability. It is UL listed and available in natural and black.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Unannealed; ISO 75-2/A |
| Solvay Specialty Polymers Ixef® 5002 Polyarylamide (PARA), 20% GlassPTFE
(discontinued **) Ixef 5002 is a 20% glass-fiber reinforced, PTFE modified polyarylamide which exhibits very good mechanical performance, very good surface gloss, and superior wear properties.- Natural: Ixef 5002/008.. |
|||