BASF Ultrason® E 2010 G4 MR SW 15102 20% Glass Filled PESU
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 20%Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultrason® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultrason® E 2010 G4 MR SW 15102 20% Glass Filled PESU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.700 - 0.800 g/cc | 0.0253 - 0.0289 lb/in³ | |
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Water Absorption | 1.6 % | 1.6 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.60 % | 0.60 % | 23°C; 50% RH; ISO 62 |
| Viscosity Measurement | 56 | 56 | [cm<sup>3</sup>/g]; ISO 307 |
| Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | ISO 2577, 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0061 cm/cm | 0.0061 in/in | ISO 2577, 294-4 |
| Melt Flow | 43.5 g/10 min @Load 10.0 kg, Temperature 360 °C |
43.5 g/10 min @Load 22.0 lb, Temperature 680 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 205 MPa @Load 98.0 kg, Time 30.0 sec |
29700 psi @Load 216 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 |
| Tensile Modulus | 7.30 GPa | 1060 ksi | ISO 527-1/-2 |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | 4.70 J/cm² | 22.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 75-1/-2 |
| 23.0 µm/m-°C @Temperature 180 °C |
12.8 µin/in-°F @Temperature 356 °F |
DIN 53752 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Glass Transition Temp, Tg | 225 °C | 437 °F | ISO 11357-1/-2 |
| Decomposition Temperature | >= 400 °C | >= 752 °F | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper throat |
| Zone 1 | 350 °C | 662 °F | Feed zone |
| Zone 2 | 360 °C | 680 °F | Compression |
| Zone 3 | 370 °C | 698 °F | Metering-zone |
| Zone 4 | 370 °C | 698 °F | Nozzle |
| Melt Temperature | 350 - 390 °C | 662 - 734 °F | Injection molding/extrusion |
| 370 °C | 698 °F | Optimal | |
| Mold Temperature | 150 - 190 °C | 302 - 374 °F | Injection molding |
| 170 °C | 338 °F | Optimal | |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 4 hour | 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Ignition Temperature | 580-600°C | DIN 54836 |
| Primary Processing Technique | Injection molding |
Users viewing this material also viewed the following:
- KKPC Kumho RM 21L High Styrene Resin Masterbatch (HSR)
- Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Conditioned)
- Techmer ES HiFill® PA6/6 GF27 SL2 27% Glass Filled
- Teknor Apex Telcar® TL-2635D Thermoplastic Elastomer
- A. Schulman FORMION™ FI 330 Ionomer
- A. Schulman SCHULAMID® 6 GF50H 50% Glass Fiber Reinforced Nylon 6
- A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate
- 3M 3635-100 Light Enhancement Film
- 3M Scotchcal™ ElectroCut™ 7125-88 Graphic Film
- DuPont Teijin Films Mylar® WC Polyester Film, 400 Gauge
Copyright © lookpolymers.com All Rights Reserved