Lanxess Durethan® AKV 30 GIT H2.0 900116 Nylon 66, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® AKV 30 GIT H2.0 900116 Nylon 66, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, injection molding grade, 30% glass fibers, suitable for GIT (gas assisted technology), good surface finish, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.368 g/cc | 0.04942 lb/in³ | ISO 1183 |
| Water Absorption | 5.0 % | 5.0 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | Conditioned; ISO 527-1/-2 |
| 190 MPa | 27600 psi | ISO 527-1/-2 | |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 |
| 6.0 % | 6.0 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 6.60 GPa | 957 ksi | Conditioned; ISO 527-1/-2 |
| 9.20 GPa | 1330 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 855 | 855 | Puncture maximum force (N); ISO 6603-2 |
| 1043 | 1043 | Puncture maximum force, Conditioned (N); ISO 6603-2 | |
| 770 @Temperature -30.0 °C |
770 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 2.10 J | 1.55 ft-lb | ISO 6603-2 |
| 3.70 J | 2.73 ft-lb | Conditioned; ISO 6603-2 | |
| 2.00 J @Temperature -30.0 °C |
1.48 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 2.00 J @Temperature -30.0 °C |
1.48 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 |
| Vicat Softening Point | 230 °C | 446 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| HB | HB | IEC 60695-11-10 | |
| Oxygen Index | 25 % | 25 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | |
| 4.2 @Frequency 1.00e+6 Hz |
4.2 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 8.0 @Frequency 100 Hz |
8.0 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | Conditioned; IEC 60243-1 |
| 45.0 kV/mm | 1140 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.0080 @Frequency 100 Hz |
0.0080 @Frequency 100 Hz |
IEC 60250 |
| 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.070 @Frequency 1.00e+6 Hz |
0.070 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.21 @Frequency 100 Hz |
0.21 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 475 V | 475 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 66,MHR,14-100,GF30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Oceanchem Group Brominated Epoxy Oligomers-3 (BEP-3)
- IDI Composites C-206 Thermoset Polyester, Sheet
- Kinlead ML21 General Grade BOPP Matt Film (thickness: 20 µm)
- Momentive Performance Materials Siloprenâ„¢ LSR 2752 Liquid Silicone Rubber - Self-Bonding
- The Chemical Company Adipic Acid, C6H10O4
- American Elements Barium Titanate nanoparticles
- Dow Corning SILASTIC® 94-599-HC SILICONE RUBBER PART A&B
- Ametek AM 388™ Alloy (UNS C72650) TD03 3/4 Hard
- Lanxess Pocan® B 3235 XF 000000 PBT, 30% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved