SABIC Innovative Plastics LNP LUBRICOMP RFN16SXZ PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFN16SXZ PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* RFN16SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.650 % | 0.650 % | 50% RH, 24 hrs; ASTM D570 |
| 1.14 % | 1.14 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0028 cm/cm @Time 86400 sec |
0.0028 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm @Time 86400 sec |
0.013 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0134 cm/cm @Time 86400 sec |
0.0134 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | ASTM D638 |
| 162 MPa | 23500 psi | ISO 527 | |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| 3.0 % | 3.0 % | ISO 527 | |
| Tensile Modulus | 9.90 GPa | 1440 ksi | 1 mm/min; ISO 527 |
| 10.68 GPa | 1549 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 246 MPa | 35700 psi | ASTM D790 |
| 255 MPa | 37000 psi | ISO 178 | |
| Flexural Modulus | 8.41 GPa | 1220 ksi | ASTM D790 |
| 9.80 GPa | 1420 ksi | ISO 178 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.65 J/cm | 16.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 57.0 kJ/m² | 27.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J | 6.64 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.43 | 0.43 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.48 | 0.48 | ASTM D3702 Modified |
| K (wear) Factor | 320 x 10-8 mm³/N-M | 159 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 31.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 63.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 63.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 249 °C @Thickness 3.20 mm |
480 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ S KE 60A-3S1725 Thermoplastic Elastomer (TPE)
- PolyOne Edgetek® AS-20GF/000 Acrylonitrile Butadiene Styrene (ABS)
- Schott LF5 Glass
- Eifeler Coatings Technology TiN PVD Coating
- Elektro-Isola G-Etronax SI Silicone, Glass Fabric Reinforcement, White, Sheets
- Chesterton 763 Rust Transformer®
- Asahi Kasei Thermofil N-13FG-1626 13% Glass Fiber Reinforced, Heat Stabilized
- 3M P595 Teak & Glass Primer
Copyright © lookpolymers.com All Rights Reserved