- Polyram PlusTek PA823M6 Nylon 6.6 for Injection Molding, 30% Minerals Reinforced, Impact Modified
Polyram PlusTek PA823M6 Nylon 6.6 for Injection Molding, 30% Minerals Reinforced, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Mineral Filled, Impact Grade |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA823M6 Nylon 6.6 for Injection Molding, 30% Minerals Reinforced, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Minerals reinforced, impact modified Nylon 6.6 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 5.5 % | 5.5 % | ISO 62 |
| Linear Mold Shrinkage | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.5 kJ/m² | 5.95 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 11357 |
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | Continuous use |
| 200 °C | 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Eastman Heatwave CF746 Polymer (discontinued **)
- NIZHNEKAMSKNEFTEKHIM PE 6844G (446H7) High Density Polyethylene
- Petroquimica Triunfo Tritheva® TN 2007 EVA Copolymer
- SABIC Innovative Plastics LNP Lubricomp PFL34 PA 6
- Silon Taborex TA 2111 HD Catalyst Masterbatch
- Sumitomo Chemical ESPOLEX® WT485 Thermoplastic Elastomer
- ExxonMobil Mobil Rarus 1024 SHC 1000 Series
- Braskem Evateno® 3019 PE EVA Foam Copolymer
- BASF Neopolen® P 9230 K 0.04 g/cc Core density; Expanded Polypropylene (Europe)
Copyright © lookpolymers.com All Rights Reserved