SABIC Innovative Plastics LNP STAT-KON WEF42I PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON WEF42I PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* WEF42I is a compound based on PBT resin containing 10% Carbon Fiber, 20% Glass Fiber. Added features of this grade include: High Impact, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM D792 |
| 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 94.0 MPa | 13600 psi | Type I, 5 mm/min; ASTM D638 |
| 99.0 MPa | 14400 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 |
| 2.5 % | 2.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 15.83 GPa | 2296 ksi | 1 mm/min; ISO 527 |
| 21.84 GPa | 3168 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 125 MPa | 18100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 169 MPa | 24500 psi | ISO 178 | |
| Flexural Modulus | 9.99 GPa | 1450 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 10.52 GPa | 1526 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.25 J/cm | 2.34 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.10 J/cm | 13.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 134 µm/m-°C @Temperature -30.0 - 30.0 °C |
74.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 219 °C @Thickness 3.20 mm |
426 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.0 - 6.0 ohm-cm | 4.0 - 6.0 ohm-cm | ASTM D257 |
| Surface Resistance | 2.0 - 5.0 ohm | 2.0 - 5.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Polymer Industries Densetec PP Copolymer Sheet
- Custom Resins Vexel™ 3250 PBT (discontinued **)
- A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT
- A. Schulman LP552-01 Narrow Molecular Weight Copolymer, High-Density Polyethylene
- DuPont Nucrel® 1202HC Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film
- Hexcel® HexWeb® CR III 1/8-5052-.0007 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Chosun Refractories N2-2 Fireclay brick
- 3M 8901 Polyester Tape
- Honeywell Stretch-Vac® Elastomax 1000 Heat-Stabilized Blown Film (discontinued **)
Copyright © lookpolymers.com All Rights Reserved