- Solvay TECHNYL® 2412GM05-D PA66, 38% glass fiber, DRY
Solvay TECHNYL® 2412GM05-D PA66, 38% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® 2412GM05-D PA66, 38% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamid 66, reinforced with 38% of glass fiber and mineral filler, for injection molding.Available in: Asia PacificProduct Applications: TECHNYL® 2412GM05-D is used in all sectors of industry, offering good mechanical strength, low warpage, good surface aspect & heat resistance. This grade is widely used for: Automotive parts-Fan & shroud, Engine cover, Timing belt cover. This product is available in black color and in colors on request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 125 MPa | 18100 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 190 MPa | 27600 psi | ASTM D790 |
| Flexural Modulus | 9.10 GPa | 1320 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 262 °C | 504 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.800 - 3.20 mm |
HB @Thickness 0.0315 - 0.126 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 270 - 275 °C | 518 - 527 °F | |
| Front Barrel Temperature | 285 - 295 °C | 545 - 563 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 275-285°C |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GF 600 A 44 Black 13 Polyamide 6 (Nylon 6)
- PolyOne OnForce™ LFT AM-60LGF/001 Natural Polyphthalamide (PPA)
- Polimeri Europa Riblene® FM 50 Low Density Polyethylene - Blown Film Extrusion
- Global GPC-130 30% Glass Filled Polycarbonate
- Greene Tweed CHEMRAZ® 615 Perfluoroelastomer
- Iran Petrochemical (PCC) HB4265 High Density Polyethylene
- Solvay Specialty Polymers Catalyst CT/1 Polyolefin
- Tisan TISLAMID® 66 30% Glass Filled Impact Modified, Heat Stabilized Nylon 66
- Denka VINYKON W4029 PVC, W grade for equipment cords, for heat resistance
Copyright © lookpolymers.com All Rights Reserved