- Shinkong Synthetic Fibers Shinite® T102G30 PET, 30% Glass Filled, Fire Retardant
Shinkong Synthetic Fibers Shinite® T102G30 PET, 30% Glass Filled, Fire Retardant
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Shinkong Synthetic Fibers Corp |
| Trade Name | Shinite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Shinkong Synthetic Fibers Shinite® T102G30 PET, 30% Glass Filled, Fire Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information from Shinkong Synthetic Fibers Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 127 MPa | 18500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 186 MPa | 27000 psi | ASTM D790 |
| Flexural Modulus | 9.81 GPa | 1420 ksi | ASTM D790 |
| Izod Impact, Notched | 0.785 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.47 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 | 4.0 | ASTM D150 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LCF30-PPS Polyphenylene Sulfide, 30% Long Carbon Fiber Reinforced
- Omni Plastics OmniLon™ 6 PA6 GR40 NA Glass Reinforced Nylon
- Quadrant EPP Nylatron® WP PA (ASTM Product Data Sheet)
- LG Chemical LUTENE FB3000 LDPE Extrusion of Blown Film
- Solvay Specialty Polymers Catalyst CT/2-OR UV Polyolefin
- Plastics Group Polifil® RMC-20 20% Calcium Carbonate-Reinforced Polypropylene, High Impact
- Trelleborg Emerson & Cuming Stycast® XT-1122 Two-Component Epoxy Flexible Encapsulant
- ExxonMobil Enable™ 27-03CH Metallocene Polyethylene Resin (European Grade)
- Arkema Group Pebax® MX 1205 SN 01 Polyether Block Amide (PEBA) (Conditioned)
Copyright © lookpolymers.com All Rights Reserved