- CP-Polymer-Technik Wellamid® 6600 MZ 401 CP Combination Nylon 66, Dry
CP-Polymer-Technik Wellamid® 6600 MZ 401 CP Combination Nylon 66, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | CP-Polymer-Technik GmbH & Co. |
| Trade Name | Wellamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CP-Polymer-Technik Wellamid® 6600 MZ 401 CP Combination Nylon 66, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.8 - 2.5 % | 1.8 - 2.5 % | 23°C/50%RH; DIN 53495 |
| Linear Mold Shrinkage | 0.0050 cm/cm @Thickness 4.00 mm |
0.0050 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 4.00 mm |
0.0060 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 12.5 GPa | 1810 ksi | ISO 527 |
| Flexural Modulus | 10.8 GPa | 1570 ksi | DIN 52457 |
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
| Melting Point | 255 °C | 491 °F | Kofler |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 179 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 179 |
| Vicat Softening Point | 230 °C | 446 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Stufe; IEC 707 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Stufe; IEC 707 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | ISO 3915 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 243-1 |
| Dielectric Loss Index | 0.015 | 0.015 | At 1 MHz; IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | Stufe; IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 265 - 295 °C | 509 - 563 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Holding Pressure | Medium | |
| Injection Speed | Medium to High | |
| Screw Speed | Medium |
Users viewing this material also viewed the following:
- Polymer Resources PEI-G40 Polyetherimide, 40% Glass Reinforced
- SABIC Innovative Plastics Lexan® HF1110 PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® 141R PC (Europe-Africa-Middle East)
- Glastic 1120 Corrosion-Resistant Panels
- SABIC Innovative Plastics LNP LUBRICOMP RX85514 PA 66 (Asia Pacific)
- Special Metals INCONEL® 690 Nickel Superalloy, Hot Rolled Flat, 0.5 x 2.0 inch (13 x 51 mm)
- A. Schulman POLYFORT™ FPP 1285 Glass Fiber-Reinforced Copolymer Polypropylene
- ChevronTexaco Rykon® ISO 32 Oil AW
- Arkema Group KYNAR® 2501-20 Polyvinylidene Fluoride Powder
- Rogers Corporation Poron® 4701-50-20 Cellular Urethane Foam
Copyright © lookpolymers.com All Rights Reserved