- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 219 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 219 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C @Thickness 3.18 mm |
219 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Nymax™ GBF 1200 23 HS BLACK 18 Polyamide 66 (Nylon 66) Information provided by PolyOne |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| SABIC PP 510P Polypropylene Homopolymer for Fiber Applications Product Description: PP 510P is a homopolymer specially designed for fiber extrusion applications with the following features:Consistent processabilityGood thread line stabilityGood color consisten.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® PP 1393 Conductive Thermoplastic Compound PRE-ELEC® PP 1393 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a very low electrical resistivity,.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® FST3403 PC Copolymer (Asia Pacific) Lexan* FST3403 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is EN45545 R6 HL3 compliant and an ideal candidate for train interior .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| Reliance Industries Repol H033MG Polypropylene REPOL Polypropylene H033MG is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| PolyMirae Moplen HP550K Stretch/Yarn, Monofilament Grade Polypropylene Moplen HP550K is the polypropylene homopolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen HP550K is a homopolymer suitable for rope, tape, yarn, monofilament.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics GELOY XP7550 ASA+PC (Europe-Africa-Middle East) Injection molding ASA-PC Blend suitable for exterior applications featuring outdoor weatherability, toughness, good heat performance and excellent flow. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| Reliance Industries Repol H110MA Polypropylene REPOL Polypropylene H110MA is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| Flint Hills P4G4B-036 Homopolymer Polypropylene Homopolymer, UL certified, and FDA compliant.Features: Nucleated, antistat, and drug master file 9988.Applications: Injection molding: general purpose.Former Huntsman polypropylene products are now .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C @Thickness 6.40 mm |
219 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LI951 Heat Resistant ASA Description: High Heat ASAApplication: Automotive Part (Radiator Grill, Side Mirror)CAS: 26299-47-8Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| Ineos H13M-00 Polypropylene Homopolymer Grade H13M-00 is a general purpose polypropylene homopolymer for injection molding applications. It provides good long-term heat stability.Suggested fabrication methods: Injection moldingFeatures: .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| LG Chemical SEETEC H5300 Polypropylene, Homopolymer Features: Seetec H5300 is designed for the extrusion of textile yarn and monofilaments. This grade is characterized by good processability and stretchability. SEETEC H5300 meets the FDA requirement .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648-97 |
| Ipiranga Petrochem PCC 0742 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| JPJ Technologies PP PE35-1 Impact copolymer for Injection Molding PP M700R is impact copolymer of good fluidity, excellent impact resistance at low temperature, good rigid-tough balance and improves stiffness. Products made from this resin are characterized by fas.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ISO 75B |
| Lucite International Diakon® Rapide CLG 910B Enhanced Molding Acrylic Polymer Specially designed to reduce injection molding cycle times and therefore provide production cost benefits.Information provided by Lucite International |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Xenoy® 1103 PBT+PC AUTOMOTIVE. Unreinforced, impact modified PBT+PC alloy. Excellent low temperature impact and chemical resistance. Range gray, black colors. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® ABS NAT Availability: North AmericaForms: PelletsFeatures: General PurposeAppearance: Natural ColorInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | |
| Styrolution NOVODUR® P2HGV ABS, 16% Glass Fiber Injection molding grade, glass reinforced (16%).Applications: Automotive industry: instrument panels, rear light housings, internal components of domestic appliances. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | annealed; ASTM Test |
| Styrolution Terluran® GP-22 ABS Terluran GP-22 is an easy flowing grade of ABS for injection molding with high resistance to impact and heat deflection.Information provided by STYROLUTION, which is a joint venture between BASF and.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| Plastics Group Polifil® RMC-20 20% Calcium Carbonate-Reinforced Polypropylene, High Impact Polifil® RMC series compounds are high impact polypropylenes reinforced with fine particle size calcium carbonate. In addition to the highest impact possible, they possess good stiffness, heat agin.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| Plastics Group Polifil® RMC-20V 20% Calcium Carbonate-Reinforced Polypropylene, High Impact, UV Stabilized Polifil® RMC-V series compounds are high impact, UV stabilized polypropylenes reinforced with fine particle size calcium carbonate. In addition to the highest impact possible, these compounds retar.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| Washington Penn PPH2UFO Polypropylene, Unfilled Homopolymer for injection molding. Meets General Motors spec. GMP.PP.013Data provided by Washington Penn Plastic Co., Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| Entec Hypro™ PPC-T10 Copolymer Polypropylene, 10% Talc Reinforced Information provided by Entec |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| Entec Hypro™ PPH-CC30 Natural Homopolymer Polypropylene, 30% Calcium Carbonate Filled Information provided by Entec |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Annealed; ASTM Data |
| Dow Tyril® 100 SAN Data provided by Dow Chemical. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 223 ABS, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® ABS 8008 Availability: North AmericaForms: PelletsFeatures: General Purpose Appearance: Natural ColorInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CH034W Polypropylene, Homopolymer, Slit Film, LWCO COPYLENE™ CH034W is a medium flow polypropylene homopolymer resin suitable for general injection molding or extrusion applications. Applications: Housewares, Raffia/tapes/strapping. Equivalent to P.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH TS15010 H VTUV1 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||