PolyOne Nymax™ GBF 1200 23 HS BLACK 18 Polyamide 66 (Nylon 66)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Nymax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Nymax™ GBF 1200 23 HS BLACK 18 Polyamide 66 (Nylon 66).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Water Absorption | 1.0 % @Thickness 3.18 mm |
1.0 % @Thickness 0.125 in |
@ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 84.8 MPa | 12300 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Modulus | 4.65 GPa | 674 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.599 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C @Thickness 3.18 mm |
219 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C @Thickness 3.18 mm |
180 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 60.0 - 107 °C | 140 - 225 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | |
| Features | Heat Stabilized | |
| Filler / Reinforcement | Glass Bead | |
| Glass Fiber Reinforcement | ||
| Unspecified FillerReinfor., 23% Filler by Weight | ||
| Forms | Pellets | |
| Generic Material | Nylon 66 | |
| Generic Name | Polyamide 66 (Nylon 66) | |
| Regional Availability | North America | |
| South America |
Users viewing this material also viewed the following:
- Abatron UWBONDL A/B Filled Potting Compound (discontinued **)
- Huntsman MY 9663 Multifunctional Resin
- Stir SpA IN 3500 AF CZ (PVC)
- SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR (Asia Pacific)
- Samsung Cheil Industries Infino® NH-3204G PC, Glass Filled FR
- Polyplastics Freqtis® C0511A (PPS/LCP), Molding Compound
- A. Schulman PP 1467-01 Polypropylene Medium Impact Polypropylene
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR Hi-Sil 233 Filler
- Arlon 28601M015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Beijing Chemical Industry KAIFA® MN201-G30 Nylon 66 Resin
Copyright © lookpolymers.com All Rights Reserved