Reliance Industries Repol H200FG Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer	Reliance Industries
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Reliance Industries Repol H200FG Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

REPOL Polypropylene H200FG is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific catalyst system. Repol H200FG is recommended for use in fiber spinning operations, for making multifilament yarn and staple fiber. Features:Good spinning characteristicsConsistent processability at high line speedsGood color stabilityHigh tensile propertiesInformation provided by Reliance Industries

Physical Properties	Metric	English	Comments
Melt Flow	20 g/10 min @Load 2.16 kg, Temperature 230 °C	20 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	34.0 MPa	4930 psi	50mm/min; ASTM D638
Elongation at Yield	11 %	11 %	50mm/min; ASTM D638
Flexural Modulus	1.65 GPa	239 ksi	1% secant; ASTM D790A
Izod Impact, Notched	0.270 J/cm @Temperature 23.0 °C	0.506 ft-lb/in @Temperature 73.4 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	104 °C	219 °F	ASTM D648