Reliance Industries Repol H110MA Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer Reliance Industries
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Reliance Industries Repol H110MA Polypropylene.pdf
  Online Service   lookpolymers   27660005
Material Notes:
REPOL Polypropylene H110MA is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific catalyst system. Repol H110MA is recommended for injection molding processes. Repol H110MA is an ideal choice for molding rigid containers, thermowares and housewares. It is also suitable as a compounding base and blending material in furniture compound. Repol H110MA contains antistat agent that reduces static charge build-up on productsFeatures: Low static charge buildup and reduced dust pickupConsistent processabilityExcellent color and processing stabilityInformation provided by Reliance Industries
Physical Properties Metric English Comments
Melt Flow 11 g/10 min

@Load 2.16 kg,
Temperature 230 °C
11 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 36.0 MPa
5220 psi
50mm/min; ASTM D638
Elongation at Yield 10 %
10 %
50mm/min; ASTM D638
Flexural Modulus 1.65 GPa
239 ksi
1% secant; ASTM D790A
Izod Impact, Notched 0.270 J/cm

@Temperature 23.0 °C
0.506 ft-lb/in

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 104 °C
219 °F