- A. Schulman ComAlloy Hiloy® 223 ABS, Glass Reinforced
A. Schulman ComAlloy Hiloy® 223 ABS, Glass Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 223 ABS, Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength, Ultimate | 93.0 MPa | 13500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 7.30 GPa | 1060 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.94 J/cm | 5.51 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 235 - 266 °C | 455 - 511 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® PPC4704 PC (Europe-Africa-Middle East)
- PTS Tristar® PC-10FR 12 MFI Flame Retardant Polycarbonate With Release
- Multibase Multi-Flex® D 4201 TPE Thermoplastic Elastomer
- Samsung Cheil Industries Starex® GR-5020T SAN, 20% Glass Filled
- A. Schulman POLYBATCH™ Red LL50283/3 Concentrate Based In LLDPE
- Covestro Bayblend® T65 AT PC/ABS Blend
- DSM Novamid® 2320J PA666
- Chesterton 752 Cold Galvanizing Compound
- Ashley Polymers Ashlene® E126 PET Polyester, 30% Glass Reinforced
- 3M 7880 Computer-Imprintable Polyester Label Material
Copyright © lookpolymers.com All Rights Reserved