- Samsung Cheil Industries Starex® GR-5020T SAN, 20% Glass Filled
Samsung Cheil Industries Starex® GR-5020T SAN, 20% Glass Filled
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® GR-5020T SAN, 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 14 g/10 min @Load 10.0 kg, Temperature 220 °C |
14 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 108 MPa | 15700 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 108 MPa | 15600 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 6.28 GPa | 910 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 6.86 GPa | 996 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm @Thickness 6.35 mm |
0.937 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.510 J/cm @Thickness 3.17 mm |
0.955 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C @Thickness 6.40 mm |
219 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C @Thickness 6.40 mm |
216 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 104 °C | 219 °F | B/50; ISO R306 |
| 107 °C | 225 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL8483 PC COPOLYMER (Asia Pacific)
- DuPont Performance Polymers Delrin® 527UV BK701 Acetal Homopolymer (Unverified Data**)
- Indium Corp. Indalloy® 164 Pb-In-Ag Solder Alloy
- Solvay TECHNYL® B 218 V30 Black 21 N PA66, 30% glass fiber, Conditioned
- SABIC Innovative Plastics Valox® 312 PBT
- Styrolution Terblend® N NM-11 ABS/PA6 (Dry)
- Techmer ES Electrablend® PA6/6 03001 Carbon Filled
- Tra-Con Tra-Bond FS227 Thixotropic Epoxy/Polyamide Adhesive
- A. Schulman ComAlloy Hiloy® 125 Polypropylene, Glass Reinforced, Chemically Coupled
- ExxonMobil Escorene® HD-8660 HDPE, Rotational Molding Pellets (discontinued **)
Copyright © lookpolymers.com All Rights Reserved