Ineos H13M-00 Polypropylene Homopolymer

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Ineos Olefins & Polymers USA
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ineos H13M-00 Polypropylene Homopolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Grade H13M-00 is a general purpose polypropylene homopolymer for injection molding applications. It provides good long-term heat stability.Suggested fabrication methods: Injection moldingFeatures: Long-term heat agingTypical applications: Packaging, Closures, Consumer productsComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from injection molded samples.

Physical Properties	Metric	English	Comments
Density	0.886 - 0.926 g/cc	0.0320 - 0.0335 lb/inÂ³	ASTM D1505
Water Absorption	<= 0.010 %	<= 0.010 %	24 hours; ASTM D570
Linear Mold Shrinkage	0.010 - 0.025 cm/cm	0.010 - 0.025 in/in	ASTM D955
Melt Flow	13.5 g/10 min @Load 2.16 kg, Temperature 230 Â°C	13.5 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	79 - 108	79 - 108	Normal range for injection molding resins; ASTM D785
Tensile Strength, Yield	37.0 MPa	5370 psi	ASTM D638
Elongation at Break	>= 200 %	>= 200 %	ASTM D638
Elongation at Yield	8.0 %	8.0 %	ASTM D638
Flexural Modulus	1.59 GPa	231 ksi	ASTM D790A
Izod Impact, Notched	0.200 - 0.300 J/cm @Diameter 3.17 mm	0.375 - 0.562 ft-lb/in @Diameter 0.125 in	bar; ASTM D256

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	100 Â°C	212 Â°F	UL Relative Thermal Index
Deflection Temperature at 0.46 MPa (66 psi)	104 Â°C	219 Â°F	ASTM D648
Flammability, UL94	HB	HB

Descriptive Properties	Value	Comments
Process	Injection Molding
Region	Mexico	Bamberger Polymers Distribution