SABIC Innovative Plastics LNP STAT-KON AE006 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON AE006 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* AE006 is a compound based on ABS containing 30% Carbon Fiber. Added feature of this grade is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.180 % | 0.180 % | 50% RH, 24 hrs; ASTM D570 |
| 0.330 % | 0.330 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00020 - 0.00040 cm/cm @Time 86400 sec |
0.00020 - 0.00040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 128 MPa | 18600 psi | 5 mm/min; ISO 527 |
| 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| 1.1 % | 1.1 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 18.64 GPa | 2704 ksi | 1 mm/min; ISO 527 |
| 20.0 GPa | 2900 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 182 MPa | 26400 psi | ISO 178 |
| 190 MPa | 27600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 17.6 GPa | 2550 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 17.6 GPa | 2550 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.14 J/cm | 5.88 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
18.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 100 °C @Thickness 3.20 mm |
212 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.0 - 4.0 ohm | 1.0 - 4.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- SYNTHOS Kralex® 1502 Styrene Butadiene Rubber
- ExxonMobil 832 Mobil DTE 800 Series
- A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer
- Elgiloy® Co-Cr-Ni Alloy, Strip, 85% Cold Reduction, Heat Treated
- EMS-Griltech Griltex® D 1441E Copolyester Hotmelt Adhesive (Technical Applications)
- DuPont Teijin Films Mylar® 75 OL Polyester Film, 75 Gauge
- BASF Pluracol® 9346 Rigid Polyol
- Overview of materials for Low Density Polyethylene (LDPE), Molded
- BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- DuPont Teijin Films Melinex® ST557 Polyester Film, 200 Gauge
Copyright © lookpolymers.com All Rights Reserved