- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 165 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 165 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Lexan® FXM4701 PPC (Asia Pacific) LEXAN FMX4701 is a high heat resistant poly(ester)carbonate injection molding resin. This grade is especially designed to visualize color effects.This data was supplied by SABIC-IP for the Asia Paci.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | DIN 53461; ASTM D648 |
| Kolon SPESIN® KP212VO Flame Retardant PBT Resin
(discontinued **) SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High hea.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 150 NC010 Acetal Homopolymer
(Unverified Data**) Delrin® 150 NC010 is a high viscosity acetal homopolymer for extrusion processes. It has excellent thermal stability, low die deposit, and enhanced crystallization for low porosity.Information pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® FG500TL NC010 Acetal Homopolymer
(Unverified Data**) Delrin® FG500TL medium viscosity acetal homopolymer resin containing 1.5% Teflon® PTFE Micropowder. It has been developed for consideration into applications such as parts for the food industry.In.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
| LATI LATAN 13 G/303 30% Glass Fiber Reinforced Polyoxymethylene Copolymer (POM)
(discontinued **) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® 12-033
(discontinued **) PRE-ELEC 12-033 is a conductive thermoplastic compound based on a polyacetal copolymer with 30% carbon fiber. PRE-ELEC 12-033 exhibits excellent mechanical properties and electrical conductivity. Te.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C @Thickness 6.40 mm |
329 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUCEL GC240 POM+GF40%, High Rigidity Feature: Injection Molding, POM+GF40%, High RigidityApplication: Casings of Pump and Pivot BearingsCAS No. 66455-31-0 and 65997-17-3Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
| LG Chemical LUCEL MR-310 Low Warpage POM, 10% Mineral Filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
| Kolon KOCETAL® GF705 G/F Reinforced Acetal Resin Glass fiber reinforced, improved stiffnessApplications: Products for high stiffness, improved fatigue properties. Information provided by API-Kolon. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| Lanxess Pocan® KU 1-7635 POS151 000000 PBT + PC, 30% Glass Fiber PBT+PC, 30% glass fibers, injection molding, low tendency to warp, improved surface finish, UV-stabilized |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| Lanxess Pocan® C 3230 XF 000000 PBT + PC, 30% Glass Fiber PBT+PC, 30% glass fibers, injection molding, improved flowability, low tendency to warp, improved surface finish |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® V3500EX PBT (Europe-Africa-Middle East) Unfilled PBT,Flame Retardant, good flow, high elongation at break for Extrusion applications (Monofilaments, Insulation Cables),Electrical Parts and Connectors |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP 5C003 FP-V (PVDF) LNP THERMOCOMP* 5C003 is a compound based on Polyvinylidene Fluoride resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 |
| Polyram RamTal PMH2022 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 22.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 |
| Polyram RamTal PMH2017 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 1.7.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | no load specified; ASTM D648 |
| Formosa Plastics Formolon® AW02 Homopolymer/Compound Homopolymer/Compound Formolon (AW02) is a NSF approved medium molecular weight dry blend PVC compound. This compound has been engineered primarily for rigid extrusion applications. The exceptional .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® BS EC PA6 Product description: Grilon BS 23 is an unreinforced, low viscosity and fine crystalline PA 6 injection molding grade. Grilon BS 23 has the following important properties: Good flow behaviorEasy pro.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| DSM Arnite® T06 200 (extrusion) PBT (European and Asian Grade) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-2 |
| BASF Ultradur B 2550 PBT Ultradur B2550 is an unfilled, very free-flowing grade for coating paper and board with high heat resistance, for example for packaging of frozen goods and ready-prepared meals. Also suitable for in.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 |
| BASF Ultramid® 8202C PA6 (Dry) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 -1 & -2 flat |
| Asahi Kasei Tenac® 4010 Homopolymer Acetal Resin General purpose grade, high impact, high elongation, medium viscosityInformation provided by Asahi Kasei Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-2 |
| BASF Ultradur B 4500 PBT Ultradur B4500 is a general-purpose injection molding grade for high-precision, high-toughness, and dimensionally stable engineering parts. It conforms to FDA requirements of 21 CFR 177.1660. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
| Cheng Yu Plastic FV30G30 POM, 30% Glass Fiber |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| DSM Arnite® T06 202 /A PBT Medium Viscosity, Injection Molding |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® 12-034
(discontinued **) PRE-ELEC 12-034 is a conductive thermoplastic compound based on a polyacetal copolymer with 40% carbon fiber. PRE-ELEC 12-034 exhibits excellent mechanical properties and electrical conductivity. Te.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | |
| LATI Lastane 50 G/25 PUR, 25% Glass Fiber Reinforced Polyurethane (PUR) based compound. Glass fibers. Very good noise reduction. Good impact resistance even at low temperature.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; No.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
| Chang Chun Plastic PBT2000 Fire Retardant PBT Information provided by Dowell Trading Company Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| DSM Arnite® T06 204 SN PBT (European and Asian Grade) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
| E-Polymers TEKAFIN® PH50GM 30% Glass Fiber Reinforced Mineral Filled Low Warpage Compounded-PP Modified PP: TEKAFIN is modified PP resins formulated with various fillers and modifiers. It has product lines for impact modified, glass fiber reinforced, inorganic filler reinforced and hybrids.I.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | |
| Radici Radiflam® S AE (cond.) Nylon 6 Radiflam® S is a range of flame retardant polyamides 6 (PA 6) used for injection molding and extrusion for all applications where high fire resistance is required.Information provided by Radici gro.. |
|||