- Cheng Yu Plastic FV30G30 POM, 30% Glass Fiber
Cheng Yu Plastic FV30G30 POM, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced |
| Manufacturer | Cheng Yu Plastic Company Limited (formerly Luen Cheong Hong) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cheng Yu Plastic FV30G30 POM, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.015 cm/cm | 0.0050 - 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 83 | 83 | ASTM D785 |
| Tensile Strength, Yield | 67.7 MPa | 9810 psi | ASTM D638 |
| Flexural Yield Strength | 211 MPa | 30600 psi | ASTM D790 |
| Izod Impact, Notched | 0.412 J/cm | 0.771 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DFL34H PC
- Kazanorgsintez E-3 Petroleum Resin
- Sax Polymers SAXLAC 320U Acrylonitrile Butadiene Styrene
- UBE UBESTA® 3030U Nylon 12 (After Zinc chloride aq. for 1000 hours)
- DuPont Performance Polymers Hytrel® BM6574 BK316 TPC-ET (Unverified Data**)
- Chosun Refractories CTL CGB-B Monolithic Refractories for Ladle and Tundish
- Clariant Renol PA233HT Nylon 6, Improved Processability, Easily Colorable, Highly Toughened
- Dow Tyrin® CM0730 Formulation
- Arlon 19566R025 0.025" (0.635 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Polyplastics Duracon® GH-25 Acetal Co-polymer (POM), GF 25% reinforced, High strength, High rigidity
Copyright © lookpolymers.com All Rights Reserved