Premix Thermoplastics PRE-ELEC® 12-034 (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Premix Thermoplastics PRE-ELEC® 12-034
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PRE-ELEC 12-034 is a conductive thermoplastic compound based on a polyacetal copolymer with 40% carbon fiber. PRE-ELEC 12-034 exhibits excellent mechanical properties and electrical conductivity. Test Specimen - 4.0 mm thick, 10.0 mm wide molded rod.Information provided by Premix Thermoplastics Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | |
| Linear Mold Shrinkage | 0.0010 - 0.0015 cm/cm | 0.0010 - 0.0015 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 97.0 MPa | 14100 psi | ISO 527 |
| Elongation at Break | 1.0 % | 1.0 % | ISO 527 |
| Tensile Modulus | 23.0 GPa | 3340 ksi | ISO 527 |
| Izod Impact, Notched | 0.420 J/cm @Thickness 4.00 mm, Temperature 23.0 °C |
0.787 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F |
ISO 180 |
| Izod Impact, Unnotched | 2.60 J/cm @Thickness 4.00 mm, Temperature 23.0 °C |
4.87 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F |
ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75/Method Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | ISO 75/Method Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 1.0 ohm-cm | <= 1.0 ohm-cm | ISO D-257 |
| Surface Resistance | <= 100 ohm | <= 100 ohm | ISO D-257 |
| Static Decay | <= 2.0 sec | <= 2.0 sec | ISO IEC 61340-5-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 185 - 210 °C | 365 - 410 °F | |
| Mold Temperature | 80.0 - 105 °C | 176 - 221 °F | |
| Drying Temperature | 80.0 °C @Time 10800 - 14400 sec |
176 °F @Time 3.00 - 4.00 hour |
Pre-drying in a dehumidifier |
| Injection Pressure | 60.0 - 80.0 MPa | 8700 - 11600 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | Moderate |
Users viewing this material also viewed the following:
- Fine Organics FINALUX G 748 Lubricant Additive
- Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F)
- Special Metals DURANICKEL® 301 (UNS N03301) Annealed Strip
- Saint-Gobain Chemlam® RL® RL7000 PTFE-Coated Polyester/Cotton Blend Reinforced Laminate
- Techmer ES HiFill® PA4/6 GF30 HS NAT 30% Glass Filled (Conditioned)
- Covestro Apec® 2097 Polycarbonate
- Chosun Refractories 1400BOARD Board
- 3M Scotch® 231 Performance Masking Tape
- Bhansali Engineering Abstron AN450M Flame Retardant ABS
Copyright © lookpolymers.com All Rights Reserved