Polyram RamTal PMH2022 Polyacetal Homopolymer for Injection Molding
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PMH2022 Polyacetal Homopolymer for Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose polyacetal homopolymer for injection molding applications, MFI 22.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ISO 2577 |
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 190 °C |
22 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ISO 527 |
| Elongation at Break | 35 % | 35 % | ISO 527 |
| Tensile Modulus | 3.40 GPa | 493 ksi | ISO 527 |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ U 5370A-E0077 Thermoplastic Elastomer (TPE)
- Pau Tai Unistab BZ-532 Mixed Metal Liquid Stabilizer for PVC Barium/Zinc Self-Lubricating
- GEHR Plastics ECTFE Polyethylene Chlorotrifluoroethylene
- Solvay Chemicals CASO® FOOD FLAKES Food additive E 509, Calcium Chloride
- SABIC Innovative Plastics LNP Stat-kon EX08308C PEI (Asia Pacific)
- Techmer ES HiFill® PA6 IM 0240 Impact Modified
- Chosun Refractories CT-140 Fireclay Castables
- Akzo Nobel Trigonox® A-80 Polymerization Initiator
- Ashley Polymers Ashlene® D925LH-30G Nylon 12, 30% Glass Reinforced, Lubricated
- ACC EP MAP-Z 10 EPI Engineered Polymers Aliphatic Polymer
Copyright © lookpolymers.com All Rights Reserved